POM Delrin® II100 NC010 DUPONT USA

Unit Price:
$3840 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
45.5MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	TD	ISO294-4	1.8	%
Modeling Shrinkage	Modeling Shrinkage	MD	ISO294-4	2.2	%
Moisture Absorption	Saturation,23°C,2.00mm	ISO62	0.90	%
Moisture Absorption	Moisture Absorption	Equilibrium,23°C,2.00mm,50%RH	ISO62	0.20	%
MediumDensity			1.19	g/cm³
SpecificHeatCapacityofMelt			3000	J/kg/°C
Melt Mass-Flow Rate		ISO1133	2.3	g/10min
Melt Volume flow Rate	190°C/2.16kg	ISO1133	1.90	cm3/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Creep Modulus	1hr	ISO899-1	2900	Mpa
Nominal Tensile Strain at Break		ISO527-2	45	%
Flexural Stress	3.5%Strain	ISO178	79.0	Mpa
Compressive Stress		ISO604	110	Mpa
Tensile Stress	Yield	ISO527-2	72.0	Mpa
Tensile Strain	Yield	ISO527-2	26	%
Tensile Creep Modulus	1000hr	ISO899-1	1600	Mpa
Tensile Modulus		ISO527-2	3000	Mpa
Flexural Modulus		ISO178	2900	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	160	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	100	°C
Vicat Softening Temperature	--	ISO306/A50	175	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO306/B50	160	°C
Linear thermal expansion coefficient	MD：-40to23°C	ISO11359-2	1E-04	cm/cm/°C
	Linear thermal expansion coefficient	TD：--	ISO11359-2	1.1E-04	cm/cm/°C
		Linear thermal expansion coefficient	TD：-40to23°C	ISO11359-2	1E-04	cm/cm/°C
			Linear thermal expansion coefficient	TD：AnnealingTemperature	ISO11359-2	160	°C
				Linear thermal expansion coefficient	TD：AnnealingTime-Optional	ISO11359-2	30.0	min/mm
					Linear thermal expansion coefficient	TD：EffectiveThermalDiffusivity	ISO11359-2	1E-07	m²/s
					Linear thermal expansion coefficient	Linear thermal expansion coefficient	MD：--	ISO11359-2	1.1E-04	cm/cm/°C
Melting Temperature		ISO11357-3	178	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface Resistivity		IEC60093	3E+13	ohms
Volume Resistivity		IEC60093	>1.0E+15	ohms·cm
Dielectric Strength		IEC60243-1	41	KV/mm
Dissipation Factor?	100Hz	IEC60250	1E-03
Dissipation Factor?	Dissipation Factor?	1MHz	IEC60250	5.5E-03
Relative Permittivity	100Hz	IEC60250	3.90
Relative Permittivity	Relative Permittivity	1MHz	IEC60250	3.80
Comparative Tracking Index		IEC60112	600	V

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	430	kJ/m²
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	NoBreak

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	M-Sale	ISO2039-2	90
Rockwell Hardness	Rockwell Hardness	R-Sale	ISO2039-2	121

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.8mm	UL94	HB
	UL flame retardant rating	1.5mm	UL94	HB
		UL flame retardant rating	0.8mm	IEC60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	1.5mm	IEC60695-11-10,-20	HB
FMVSS Flammability		FMVSS302	B
atomization	F-value(refraction)	ISO6452	91	%
atomization	atomization	G-value(condensate)	ISO6452	1E-04	g
Burning Rate	1.00mm	ISO3795	30	mm/min

Supplementary information	Test Condition	Test Method	Test Result	Unit
Emission		VDA275	<8.00	mg/kg
EmissionofOrganicCompounds		VDA277	4.00	µgC/g

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.