Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD | ISO294-4 | 1.5 | % |
Modeling Shrinkage | MD | ISO294-4 | 1.2 | % |
Moisture Absorption | Saturation,23°C | ISO62 | 0.50 | % |
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.20 | % |
Melt Volume flow Rate | 190°C/2.16kg | ISO1133 | 12.0 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Nominal Tensile Strain at Break | | ISO527-2/50 | 50 | % |
Tensile Stress | Yield | ISO527-2/50 | 22.0 | Mpa |
Tensile Strain | Yield | ISO527-2/50 | 25 | % |
Tensile Modulus | | ISO527-2 | 700 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 55.0 | °C |
Linear thermal expansion coefficient | MD:23to55°C | ISO11359-2 | 1.4E-04 | cm/cm/°C |
Melting temperature | | ISO11357-3 | 164 | °C |
Maximum Service Temperature (short cycle operation) | | | 100 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dissipation Factor? | 1MHz | IEC60250 | 0.026 | |
Dielectric Strength | | IEC60243-1 | 85 | KV/mm |
Relative Permittivity | 1MHz | IEC60250 | 5.00 | |
Comparative Tracking Index | SolutionA | IEC60112 | 600 | V |
Surface Resistivity | | IEC60093 | 1E+12 | ohms |
Volume Resistivity | | IEC60093 | 1E+13 | ohms·cm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 无断裂 | |
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 无断裂 | |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Ball Indentation Hardness | H132/30 | ISO2039-1 | 30.0 | Mpa |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 1.6mm | UL94 | HB | |
Supplementary information | Test Condition | Test Method | Test Result | Unit |
---|
ISO Type | | 3.38 | POM-K,M-GNPR,04-001 | |
AutomotiveMaterials | >1.00mm | FMVSS302 | Pass | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.