Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | Equilibrium, 23°C, 60% RH | ASTM D570 | 0.21 | % |
| Melt Mass-Flow Rate | 190°C/2.16 kg | ASTM D1238 | 9.0 | g/10 min |
| Modeling Shrinkage - Flow | | ASTM D955 | 1.8 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Strength | 23°C | ASTM D638 | 55.0 | Mpa |
| Tensile Elongation | Break, 23°C | ASTM D638 | 40 | % |
| Flexural Modulus | 23°C | ASTM D790 | 2700 | Mpa |
| Flexural Strength | 23°C | ASTM D790 | 86.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melting temperature | | ASTM D1525 | 166 | °C |
| Coefficient of Linear Thermal Expansion (Flow) | | ASTM D696 | 1.3E-5 | cm/cm/°C |
| Deflection Temperature Under Load? | 0.45 MPa, Unannealed | ASTM D648A | 160 | °C |
| Deflection Temperature Under Load? | 1.8 MPa, Unannealed | ASTM D648A | 130 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dissipation Factor? | 1 MHz | ASTM D150 | 6.0E-3 | |
| Dielectric Strength | | ASTM D149 | 19 | KV/mm |
| Surface Resistivity | | ASTM D257 | 1.0E+16 | ohms |
| Dielectric Constant | | ASTM D150 | 3.70 | |
| Volume Resistivity | | ASTM D257 | 1.0E+14 | ohms·cm |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | M-Scale | ASTM D785 | 82 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating | | UL 94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.