Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1.400 | |
Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.8 | % |
Melt Mass-Flow Rate | | ASTM D1238/ISO 1133 | 7.5 | g/10min |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | 23C/50RH | ISO 62 | 0.20 | |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Elongation?(Break) | | ASTM D638/ISO 527 | 27 | % |
Tensile Modulus | | ASTM D638/ISO 527 | 2700 | kg/cm²(MPa)[Lb/in²] |
Tensile Modulus | 73℉ | ISO 527-1,-2 | 392000 | psi |
Tensile Strength | | ASTM D638/ISO 527 | 65 | kg/cm²(MPa)[Lb/in²] |
Flexural Modulus | | ASTM D790/ISO 178 | 1800 | kg/cm²(MPa)[Lb/in²] |
Tensile Stress(Yield) | 73℉ | ISO 527-1,-2 | 9430 | psi |
Tensile Strain(Yield) | 73℉ | ISO 527-1,-2 | 9.0 | % |
Tensile Creep Modulus | 1000h | ISO 899-1 | 189000 | psi |
Charpy Notched Impact Strength | -22℉ | ISO 179 | 2.38 | ft·lb/in |
Charpy Notched Impact Strength | 73℉ | ISO 179 | 2.62 | ft·lb/in |
Charpy Unnotched Impact Strength | -22℉ | ISO 179 | 80.9 | ft·lb/in |
Charpy Unnotched Impact Strength | 73℉ | ISO 179 | 85.7 | ft·lb/in |
Izod notch impact strength | | ASTM D256/ISO 179 | 6 | kg·cm/cm(J/M)ft·lb/in |
Charpy impact strength | | ASTM D256/ISO 179 | 3.8 | kg·cm/cm(J/M)ft·lb/in |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flame retardancy | | UL94 | HB | |
Melting temperature | | ISO 3146 | 333 | ℉ |
Deflection Temperature Under Load? | 1.80MPa | ISO 75A-1,-2 | 212 | ℉ |
Melting Temperature | | | 167 | ℃(℉) |
Vicat Softening Temperature | | ASTM D1525/ISO R306 | 150 | ℃(℉) |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC 60093 | 1E+13 | ohms |
Volume Resistivity | | IEC 60093 | 1E+15 | ohm·cm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.