Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | Equilibrium,23°C,60%RH | ASTMD570 | 0.22 | % |
| -- | | ISO1133 | 5.0 | g/10min |
| Density / Specific Gravity | | ASTMD792,ISO1183 | 1.40 | g/cm³ |
| 190°C/2.16kg | | ASTMD1238 | 5.0 | g/10min |
| 流动:3.00mm | | ASTMD955 | 2.0 | % |
| 3.00mm | | ASTMD955 | 2.0 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| 23°C | | ASTMD790 | 2500 | Mpa |
| 23°C | | ISO178 | 2550 | Mpa |
| 23°C | | ASTMD790 | 82.0 | Mpa |
| 23°C | | ISO178 | 86.0 | Mpa |
| Field, 23°C | | ASTMD638 | 60.0 | Mpa |
| Field, 23°C | | ISO527-2 | 64.0 | Mpa |
| Coefficient of Friction | 与金属-动态 | ASTMD1894 | 0.27 | |
| Coefficient of Friction | Itself - Dynamic | ASTMD1894 | 0.22 | |
| Tensile Elongation | Break,23°C | ASTMD638 | 60 | % |
| Nominal Tensile Strain at Break | 23°C | ISO527-2 | 40 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| 0.45MPa, Unannealed | | ASTMD648 | 158 | °C |
| 1.8MPa, Unannealed | | ASTMD648 | 110 | °C |
| 1.8MPa, Unannealed | | ISO75-2/A | 97.0 | °C |
| Linear thermal expansion coefficient | MD：20to80°C | ASTMD696 | 1.3E-04 | cm/cm/°C |
| Peak Melting Temperature | | ASTMD3418 | 165 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface Resistivity | | ASTMD257,IEC60093 | 1E+16 | ohms |
| Volume Resistivity | | ASTMD257,IEC60093 | 1E+14 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 7.5 | kJ/m² |
| Notched Izod Impact Strength | 3.20mm | ASTMD256 | 78 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | M-Scale | ASTMD785 | 80 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.800mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.