POM LNP™ LUBRICOMP™ KD000 BKANT SABIC INNOVATIVE US
104
- Unit Price:
- $3421 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 59.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:heat-resisting high strength Glass fiber reinforced
- Application Areas:Automotive Applications
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD:24hr | ISO294-4 | 1.5to3.5 | % |
| MD:24hr | ISO294-4 | 1.5to3.5 | % | |
| MD：60°C | 内部方法 | 1.2to1.3 | % | |
| MD：100°C | 内部方法 | 1.5to1.6 | % | |
| MD：24hr | ASTMD955 | 1.5to3.5 | % | |
| TD：60°C | 内部方法 | 0.90to1.0 | % | |
| TD：100°C | 内部方法 | 1.1to1.2 | % | |
| TD：24hr | ASTMD955 | 1.5to3.5 | % | |
| Water absorption rate | 24hr,50%RH | ASTMD570 | 0.28 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.33 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Break | ISO527-2 | 47.0 | Mpa |
| Yield | ISO527-2 | 53.0 | Mpa | |
| Tensile strain | Break | ISO527-2 | 20 | % |
| Yield | ISO527-2 | 5.0 | % | |
| Tensile modulus | ISO527-2/1 | 3000 | Mpa | |
| elongation | Break | ASTMD638 | 7.2 | % |
| Yield | ASTMD638 | 3.6 | % | |
| Bending modulus | ASTMD790 | 3250 | Mpa | |
| ISO178 | 3200 | Mpa | ||
| bending strength | ASTMD790 | 95.0 | Mpa | |
| Tensile strength | Yield | ASTMD638 | 58.0 | Mpa |
| Break | ASTMD638 | 54.0 | Mpa | |
| Bending stress | ISO178 | 82.0 | Mpa | |
| Tensile modulus 2 | ASTMD638 | 3500 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 108 | °C |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 1E-04 | cm/cm/°C |
| MD：-40to40°C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 1E-04 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| Hot deformation temperature 4 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 105 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | ASTMD257 | 1.0E+2to1.0E+4 | ohms |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Suspended wall beam gap impact strength 3 | 23°C | ISO180/1A | 5.0 | kJ/m² |
| UnnotchedIzodImpactStrength3 | 23°C | ISO180/1U | 37 | kJ/m² |
| Dart impact equipped with measuring instruments | 23°C,EnergyatPeakLoad | ASTMD3763 | 5.00 | J |
| Multi axis Instrumented Impact Energy | ISO6603-2 | 1.50 | J |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | 0.70mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.