Technical Data Sheet
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Strength | Yield,23℃ | MPa | ASTM D638 | |
| Flexural Modulus | 23°C | MPa | ASTM D790 | 6680 |
| Flexural Strength | 23°C | MPa | ASTM D790 | 157 |
| IZOD Notch Impact Strength | 3.20mm | J/m | ASTM D256 | 57.0 |
| Tensile Elongation?(Break) | Break,23℃ | % | ASTM D638 | 2.0 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Thermal distortion temperature | 1.8MPa,Unannealed | °C | ASTM D648 | 164 |
| Melting temperature | | °C | ASTM D3418 | |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface Resistivity | | ohms | ASTM D257 | |
| Volume Resistivity | | ohm·cm | ASTM D257 | |
| Other | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating | 0.8mm | | UL 94 | HB |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Density / Specific Gravity | | g/cm³ | ASTM D792 | 1.58 |
| Melt Mass-Flow Rate | 190℃/2.16kg | g/10 min | ASTM D1238 | |
| Modeling Shrinkage | flow,2.00MM | % | ASTM D955 | 0.50 |
| Moisture Absorption | Equilibrium,23℃,60%rh | % | ASTM D570 | 0.20 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.