POM LNP™ LUBRICOMP™ KF006 BK SABIC INNOVATIVE US
90
- Unit Price:
- $3014 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 40MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:heat-resisting high strength Glass fiber reinforced
- Application Areas:Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Flow | 内部方法 | 0.50 到 0.80 | % |
| Across Flow | 内部方法 | 0.80 到 1.1 | % | |
| Water absorption rate | 24 hr, 23°C | ISO 62 | 0.40 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Yield | ISO 527-2/5 | 125 | Mpa |
| Tensile strain | Break | ISO 527-2/5 | 2.9 | % |
| Bending modulus 2 | ISO 178 | 7400 | Mpa | |
| Bending stress 2, 3 | ISO 178 | 163 | Mpa | |
| Tensile modulus | ISO 527-2/1 | 9200 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature 4 | 0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span | ISO 75-2/Bf | 164 | °C |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span | ISO 75-2/Af | 161 | °C | |
| Linear coefficient of thermal expansion | Flow : 23 to 60°C | ISO 11359-2 | 3.2E-5 | cm/cm/°C |
| Across Flow : 23 to 60°C | ISO 11359-2 | 9.6E-5 | cm/cm/°C |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 80 | °C | ||
| Processing (melt) temperature | 200 到 215 | °C | ||
| Mold temperature | 80 到 110 | °C | ||
| drying time | 4.0 | hr | ||
| Temperature at the rear of the barrel | 175 到 190 | °C | ||
| Temperature in the middle of the barrel | 195 到 205 | °C | ||
| Temperature at the front of the material cylinder | 210 到 220 | °C | ||
| Back pressure | 0.200 到 0.300 | Mpa | ||
| Screw speed | 30 到 60 | rpm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Unscented Izod impact strength | 23°C | ISO 180/1U | 40 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.