POM Delrin® 527UV NC DUPONT USA

Unit Price:
$8222 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
25MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Photostability Low wear Weather resistance
Application Areas:Automotive sector Automotive interior parts
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	TD	ISO294-4	1.9	%
Modeling Shrinkage	Modeling Shrinkage	MD	ISO294-4	2.0	%
Moisture Absorption	23°C,24hr	ISO62	0.50	%
	Moisture Absorption	Saturation,23°C,2.00mm	ISO62	1.2	%
	Moisture Absorption	Moisture Absorption	Equilibrium,23°C,2.00mm,50%RH	ISO62	0.20	%
Melt Mass-Flow Rate	190°C/2.16kg	ISO1133	15	g/10min
Melt Volume flow Rate	190°C/2.16kg	ISO1133	13.0	cm3/10min
Density / Specific Gravity		ISO1183	1.42	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress		ISO178	77.0	Mpa
Nominal Tensile Strain at Break		ISO527-2	30	%
Poisson Ratio		ISO527	0.37
Tensile Stress	Yield	ISO527-2	70.0	Mpa
Tensile Strain	Yield	ISO527-2	17	%
Tensile Modulus		ISO527-2	3100	Mpa
Flexural Modulus		ISO178	3000	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	163	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	95.0	°C
Vicat Softening Temperature	--	ISO306/A50	174	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO306/B50	160	°C
Linear thermal expansion coefficient	MD	ISO11359-2	1.1E-04	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD	ISO11359-2	1.2E-04	cm/cm/°C
Melting Temperature		ISO11357-3	178	°C
Annealing Temperature			160	°C
Annealing Time-Optional			30.0	min/mm

Electrical performance	Test Condition	Test Method	Test Result	Unit
Relative Permittivity	100Hz	IEC60250	3.80
Relative Permittivity	Relative Permittivity	1MHz	IEC60250	3.80
Comparative Tracking Index		IEC60112	600	V
Dissipation Factor?	100Hz	IEC60250	2.1E-03
Dissipation Factor?	Dissipation Factor?	1MHz	IEC60250	5.6E-03
Surface Resistivity		IEC60093	2E+13	ohms
Volume Resistivity		IEC60093	>1.0E+15	ohms·cm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	260	kJ/m²
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	260	kJ/m²
Charpy Notched Impact Strength	-30°C	ISO179/1eA	8.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	9.0	kJ/m²
Notched Izod Impact Strength	-40°C	ISO180/1A	8.0	kJ/m²
Notched Izod Impact Strength	Notched Izod Impact Strength	23°C	ISO180/1A	8.0	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	M-Sale	ISO2039-2	92
Rockwell Hardness	Rockwell Hardness	R-Sale	ISO2039-2	120

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.8mm	UL94	HB
UL flame retardant rating	UL flame retardant rating	0.8mm	IEC60695-11-10,-20	HB
FMVSS Flammability		FMVSS302	B
atomization	F-value(refraction)4	ISO6452	90	%
atomization	atomization	G-value(condensate)	ISO6452	2E-04	g
Burning Rate	1.00mm	ISO3795	21	mm/min

Supplementary information	Test Method	Test Result	Unit
EmissionofOrganicCompounds	VDA277	16.0	µgC/g
Odor	VDA270	6.00
Emission	VDA275	<8.00	mg/kg

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.