Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD | ASTMD955 | 2.2 | % |
Modeling Shrinkage | TD | ASTMD955 | 1.8 | % |
Modeling Shrinkage | TD | ISO294-4 | 1.8 | % |
Modeling Shrinkage | MD | ISO294-4 | 2.2 | % |
Moisture Absorption | Saturation,23°C | ISO62 | 0.75 | % |
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.20 | % |
SpecificHeatCapacityofMelt | | 内部方法 | 2210 | J/kg/°C |
ThermalConductivityofMelt | | 内部方法 | 0.16 | W/m/K |
Melt Volume flow Rate | 190°C/2.16kg | ISO1133 | 2.20 | cm3/10min |
DensityofMelt | | 内部方法 | 1.200 | g/cm³ |
Melt Mass-Flow Rate | | ASTMD1238 | 2.5 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Creep Modulus | 1hr | ISO899-1 | 2100 | Mpa |
Tensile Stress | Yield | ISO527-2/1A/50 | 63.0 | Mpa |
Tensile Strain | Yield | ISO527-2/1A/50 | 12 | % |
Tensile Strength | Yield,-40°C | ASTMD638 | 94.5 | Mpa |
Tensile Strength | Yield,23°C | ASTMD638 | 60.7 | Mpa |
Tensile Strength | Yield,71°C | ASTMD638 | 34.5 | Mpa |
Tensile Creep Modulus | 1000hr | ISO899-1 | 1100 | Mpa |
Tensile Modulus | | ISO527-2/1A/1 | 2460 | Mpa |
Flexural Modulus | 23°C | ISO178 | 2430 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ASTMD648 | 110 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 94.0 | °C |
Linear thermal expansion coefficient | MD | ISO11359-2 | 1.2E-04 | cm/cm/°C |
Linear thermal expansion coefficient | TD | ISO11359-2 | 1.2E-04 | cm/cm/°C |
Peak Melting Temperature | | ASTMD3418 | 165 | °C |
Melting Temperature | | ISO11357-3 | 166 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Volume Resistivity | | ASTMD257 | 1E+14 | ohms·cm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 190 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C,Partial Break | ISO179/1eU | 250 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.