Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD | ASTMD955 | 2.2 | % |
Modeling Shrinkage | TD | ASTMD955 | 1.8 | % |
Modeling Shrinkage | TD | ISO294-4 | 1.6 | % |
Modeling Shrinkage | MD | ISO294-4 | 1.9 | % |
Melt Volume flow Rate | 190°C/2.16kg | ISO1133 | 8.40 | cm3/10min |
Density / Specific Gravity | | ASTMD792 | 1.40 | g/cm³ |
Density / Specific Gravity | | ISO1183 | 1.38 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | | ISO527-2/1A/1 | 2500 | Mpa |
Flexural Modulus | 23°C | ISO178 | 2400 | Mpa |
Tensile Stress | Yield | ISO527-2/1A/50 | 56.0 | Mpa |
Tensile Strain | Yield | ISO527-2/1A/50 | 10 | % |
Tensile Strength | Yield,23°C | ASTMD638 | 51.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Linear thermal expansion coefficient | TD | ISO11359-2 | 1.2E-04 | cm/cm/°C |
Linear thermal expansion coefficient | MD | ISO11359-2 | 1.1E-04 | cm/cm/°C |
Peak Melting Temperature | | ASTMD3418 | 165 | °C |
Melting Temperature | | ISO11357-3 | 166 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ASTMD648 | 110 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 94.0 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Volume Resistivity | | ASTMD257 | 1E+14 | ohms·cm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Notched Impact Strength | -30°C | ISO179/1eA | 4.5 | kJ/m² |
Charpy Notched Impact Strength | 23°C | ISO179/1eA | 7.0 | kJ/m² |
Notched Izod Impact Strength | 23°C | ISO180/1A | 5.3 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.