Material Description
Technical Data Sheet
Material Description
- Material Properties:UV resistance scratch resistance wear resistant Medium viscosity
- Application Areas:Gear Engineering accessories Automotive sector Application in the automo currency Shell
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density | ASTM D792/ISO 1183 | 1.41 | ||
| Modeling Shrinkage | ASTM D955 | 1.6-2.0 | % |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Mass-Flow Rate | 190°C/2.16kg | ISO1133 | 8.0 | g/10min |
| Melt index | ISO 1133 | 8.0 | g/10 min | |
| Modeling Shrinkage | MD | Internal Method | 1.6-2.0 | % |
| MD | 内部方法 | 1.6到2.0 | % | |
| Moisture Absorption | 23°C,24hr,50%RH | ASTMD570 | 0.20 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Stress | Yield | ISO527-2 | 66.0 | Mpa |
| -- | ASTMD638 | 64.0 | Mpa | |
| Yield, 23℃ | ISO 527-2 | 69.0 | Mpa | |
| Tensile Strain | Break,23℃ | ISO 527-2 | 55 | % |
| Tensile Modulus | ASTM D638/ISO 527 | 3000(MPa) | kg/cm²(MPa)[Lb/in²] | |
| 23℃ | ISO 527-2 | 3000 | Mpa | |
| ISO527-2 | 2750 | Mpa | ||
| Tensile Elongation | Break | ASTMD638,ISO527-2 | 40 | % |
| Flexural Modulus | ASTMD790,ISO178 | 2600 | Mpa | |
| Flexural Strength | ASTMD790 | 88.0 | Mpa | |
| Charpy Notched Impact Strength | ISO 179 | 7.0 | kJ/m² |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame Rating | 0.750 mm | UL 94 | HB | |
| Specific Heat | 1470 | J/kg/°C | ||
| Thermal Conductivity | 0.23 | W/m/K | ||
| Burning Rate | UL94 | HB | ||
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ASTMD648 | 163 | °C |
| 0.45MPa,Unannealed | ISO75-2/B | 158 | °C | |
| 1.8MPa,Unannealed | ASTMD648 | 124 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 102 | °C | |
| 0.45 MPa, Unannealed | ISO 75-2/B | 158 | °C | |
| 1.8 MPa, Unannealed | ISO 75-2/A | 102 | °C | |
| Linear thermal expansion coefficient | MD | ASTMD696,ISO11359-2 | 1E-04 | cm/cm/°C |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | R-Scale | ASTMD785 | 117 | |
| M-Scale | ASTMD785 | 88 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.