Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1420 | |
Modeling Shrinkage | | ASTM D955 | 1.8 | % |
Melt Mass-Flow Rate | | ASTM D1238/ISO 1133 | 6.5 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Elongation?(Break) | 50mm/min | ISO 527 part 1/2 | 20 | % |
Tensile Modulus | 1mm/min | ISO 527 part 1/2 | 2800 | Mpa |
Tensile Elongation | 伸长率 | ISO 527 part 1/2 | 9.0 | % |
Flexural Modulus | | ISO 178 | 2700 | Mpa |
Tensile Creep Modulus | 1 hour | ISO 899 part 1 | 2400 | Mpa |
Tensile Creep Modulus | 1000 hours | ISO 899 part 1 | 1200 | Mpa |
Charpy Notched Impact Strength | 23℃ | ISO 179 1eA | 0.6 | J/cm |
Charpy Notched Impact Strength | 低温-30℃ | ISO 179 1eA | 0.6 | J/cm |
Charpy Unnotched Impact Strength | 低温-30℃ | ISO 179 1eU | 12 | J/cm |
Charpy Unnotched Impact Strength | 23℃ | ISO 179 1eU | 12.0 | J/cm |
Tensile Strength(Yield) | 50mm/min | ISO 527 part 1/2 | 65 | Mpa |
Ball Indentation Hardness | 30sec数值 | ISO 2039 part 1 | 140 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Coefficient of Linear Thermal Expansion | 23-55℃ Longitudinal | ISO 11359 part 1/2 | 110 | µm/m-℃ |
Deflection Temperature Under Load? | 1.8MPa | ISO 75 part 1/2 | 100 | °C |
Melting Temperature | DSC,10 K/min | ISO 3146 method C1b | 166 | °C |
Vicat Softening Temperature | VST/B/50 | ISO 306 | 150 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Constant | 1 MHz | IEC 60250 | 4.20 | |
Dielectric Constant | 低频100 Hz | IEC 60250 | 4.20 | |
Dissipation Factor? | | IEC 60250 | 0.008 | 1 MHz |
Dissipation Factor? | 低频100 Hz | IEC 60250 | 0.0025 | |
Insulation strength | | IEC 60243 part 1 | 35 | KV/mm |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | 23℃and50%RH | ISO 62 | 0.2 | % |
Moisture Absorption | Saturation23℃ | ISO 62 | 0.75 | % |
Melt index | 8.5cm | ISO 1133 | 12.07 | g/10min |
Density | | ISO 1183 | 1.42 | g/cm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.