Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | ASTM D792/ISO 1183 | 1.41 | |
| Modeling Shrinkage | | ASTM D955 | 2.0 | % |
| Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.2 | % |
| Melt Mass-Flow Rate | | ASTM D1238/ISO 1133 | 13 | g/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Elongation?(Break) | | ASTM D638/ISO 527 | 32 | % |
| Tensile Strength | | ASTM D638/ISO 527 | 68 | kg/cm²(MPa)[Lb/in²] |
| Tensile Elongation | | ASTM D638/ISO 527 | 10 | % |
| Flexural Modulus | | ASTM D790/ISO 178 | 2800 | kg/cm²(MPa)[Lb/in²] |
| Flexural Strength | | ASTM D790/ISO 178 | 94 | kg/cm²(MPa)[Lb/in²] |
| Charpy impact strength | | ASTM D256/ISO 179 | 6.5 | kg·cm/cm(J/M)ft·lb/in |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Burning Rate | | UL94 | HB | |
| Deflection Temperature Under Load? | | ASTM D648/ISO 75 | 101 | ℃（℉） |
| Melting Temperature | | | 168 | ℃（℉） |
| Linear expansion coefficient | | ASTM D696/ISO 11359 | 12 | mm/mm.℃ |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface Resistivity | | ASTM D257/IEC 60093 | 1x10的16次方 | Ω |
| Volume Resistivity | | ASTM D257/IEC 60093 | 1x10的14次方 | Ω.cm |
| Processing | Test Condition | Test Method | Test Result | Unit |
|---|
| Mold Temperature | | | 60~80 | °C |
| Processing temperature | | | 170 | °C |
| Processing temperature | | | 190 | °C |
| Processing temperature | | | 180 | °C |
| Processing temperature | | | 180-210 | °C |
| Drying conditions | | | 80-100C（175-210F),3-4hrs | |
| Screw Speed | | | 80~120转/分钟 | rpm |
| Pressure | | | 注射压力的50%~100% | Mpa |
| Pressure | | | 5~10kg/cm | Mpa |
| Pressure | | | 500~1200kg/cm2（7.110~17.070psi） | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.