Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | 水平方向 | | 2.1 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | 1h | | 1800 | Mpa |
Tensile Modulus | | | 2600 | Mpa |
Tensile Elongation | Break | | 29 | % |
Tensile Strength(Yield) | | | 63 | Mpa |
Tensile Elongation (Break) | | | 9.6 | % |
Charpy impact strength | 23℃ | | 200 | KJ/m |
Charpy impact strength | 23℃ | | 5.5 | KJ/m |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 1.80MPa | | 105 | °C |
Melting Temperature | 10℃/min | | 167 | °C |
Burning rate | 1.6mm | | HB | CLASS |
Coefficient of Linear Thermal Expansion | 水平方向 | | 1.1 | E-4/℃ |
Vicat Softening Temperature | 50℃/h50n | | 150 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Strength | | | 40 | KV/mm |
Surface Resistivity | | | 1E+13 | Ohm |
Dielectric Constant | 100HZ | | 3.8 | |
Volume Resistivity | | | 1E+13 | Ohm |
Other | Test Condition | Test Method | Test Result | Unit |
---|
Oxygen Index | | | 15 | % |
Taber Abrasion Resistance | 100HZ | | 10 | |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Density / Specific Gravity | | | 1400 | kg/cm |
Moisture Absorption | | | 0.2 | % |
Melt index | 220℃/10kg | | 7.5 | CM |
Moisture Absorption | | | 0.8 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.