POM LNP™ LUBRICOMP™ KL-4540D SABIC INNOVATIVE US
82
- Unit Price:
- $3528 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low extract Internal lubrication
- Application Areas:Electrical appliances Electronic display Medical and nursing suppl
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | Flow : 24hr | ASTM D955 | 2.1 到 2.9 | % |
| Across Flow : 24hr | ASTM D955 | 2.1 到 2.9 | % | |
| Moisture Absorption | 24 hr, 50% RH | ASTM D570 | 0.18 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.43 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Stress | -- | ISO 178 | 60.0 | Mpa |
| Break, 50.0 mm Span 3 | ASTM D790 | 63.0 | Mpa | |
| Tensile Modulus | -- 1 | ASTM D638 | 1830 | Mpa |
| -- | ISO 527-2/1 | 2020 | Mpa | |
| Tensile Elongation | Yield 2 | ASTM D638 | 14 | % |
| Yield | ISO 527-2/5 | 22 | % | |
| Break 2 | ASTM D638 | 30 | % | |
| Break | ISO 527-2/5 | 43 | % | |
| Flexural Modulus | 50.0 mm Span 3 | ASTM D790 | 2020 | Mpa |
| -- 4 | ISO 178 | 2080 | Mpa | |
| Tensile Strength | Yield 2 | ASTM D638 | 43.0 | Mpa |
| Yield | ISO 527-2/5 | 39.0 | Mpa | |
| Break 2 | ASTM D638 | 43.0 | Mpa | |
| Break | ISO 527-2/5 | 39.0 | Mpa | |
| Coefficient of Friction | Dynamic | ASTM D3702 | 0.25 | |
| Static | ASTM D3702 | 0.14 | ||
| Specific Wear Rate | ASTM D3702 | 1.8E+6 | 10^-8 mm³/N·m |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 87.0 | °C |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 6 | ISO 75-2/Af | 79.0 | °C | |
| Linear thermal expansion coefficient | Flow : -40 to 40°C | ASTM E831 | 1.1E-4 | cm/cm/°C |
| Across Flow : -40 to 40°C | ASTM E831 | 1.1E-4 | cm/cm/°C |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Temperature | 80 | °C | ||
| Processing (Melt) Temp | 200 到 215 | °C | ||
| Mold Temperature | 80 到 110 | °C | ||
| Drying Time | 4.0 | hr | ||
| Rear Temperature | 175 到 190 | °C | ||
| Middle Temperature | 195 到 205 | °C | ||
| Front Temperature | 210 到 220 | °C | ||
| Back Pressure | 0.200 到 0.300 | Mpa | ||
| Screw Speed | 30 到 60 | rpm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Instrumented Dart Impact | 23°C, Energy at Peak | ASTM D3763 | 3.00 | J |
| -- | ISO 6603-2 | 1.00 | J | |
| Unnotched Izod Impact Strength | 23°C | ASTM D4812 | 620 | J/m |
| 23°C 6 | ISO 180/1U | 42 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.