POM LNP™ LUBRICOMP™ KL-4540 SABIC INNOVATIVE US

Unit Price:
$4809 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
38.5MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Flow : 24hr	ASTM D955	2.1 到 2.9	%
Modeling Shrinkage	Modeling Shrinkage	Across Flow : 24hr	ASTM D955	2.1 到 2.9	%
Moisture Absorption	24 hr, 50% RH	ASTM D570	0.18	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.43	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress	--	ISO 178	60.0	Mpa
Flexural Stress	Flexural Stress	Break, 50.0 mm Span 3	ASTM D790	63.0	Mpa
Tensile Modulus	-- 1	ASTM D638	1830	Mpa
Tensile Modulus	Tensile Modulus	--	ISO 527-2/1	2020	Mpa
Tensile Elongation	Yield 2	ASTM D638	14	%
	Tensile Elongation	Yield	ISO 527-2/5	22	%
		Tensile Elongation	Break 2	ASTM D638	30	%
		Tensile Elongation	Tensile Elongation	Break	ISO 527-2/5	43	%
Flexural Modulus	50.0 mm Span 3	ASTM D790	2020	Mpa
Flexural Modulus	Flexural Modulus	-- 4	ISO 178	2080	Mpa
Tensile Strength	Yield 2	ASTM D638	43.0	Mpa
	Tensile Strength	Yield	ISO 527-2/5	39.0	Mpa
		Tensile Strength	Break 2	ASTM D638	43.0	Mpa
		Tensile Strength	Tensile Strength	Break	ISO 527-2/5	39.0	Mpa
Coefficient of Friction	Dynamic	ASTM D3702	0.25
Coefficient of Friction	Coefficient of Friction	Static	ASTM D3702	0.14
Specific Wear Rate		ASTM D3702	1.8E+6	10^-8 mm³/N·m

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	87.0	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 6	ISO 75-2/Af	79.0	°C
Linear thermal expansion coefficient	Flow : -40 to 40°C	ASTM E831	1.1E-4	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : -40 to 40°C	ASTM E831	1.1E-4	cm/cm/°C

Injection	Test Result	Unit
Drying Temperature	80	°C
Processing (Melt) Temp	200 到 215	°C
Mold Temperature	80 到 110	°C
Drying Time	4.0	hr
Rear Temperature	175 到 190	°C
Middle Temperature	195 到 205	°C
Front Temperature	210 到 220	°C
Back Pressure	0.200 到 0.300	Mpa
Screw Speed	30 到 60	rpm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	23°C, Energy at Peak	ASTM D3763	3.00	J
Instrumented Dart Impact	Instrumented Dart Impact	--	ISO 6603-2	1.00	J
Unnotched Izod Impact Strength	23°C	ASTM D4812	620	J/m
Unnotched Izod Impact Strength	Unnotched Izod Impact Strength	23°C 6	ISO 180/1U	42	kJ/m²

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.