POM HOSTAFORM® C27021 CELANESE USA
30
- Unit Price:
- $4358 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Elongation?(Break) | 50mm/min | ISO 527 part 1/2 | 17.0 | % |
| Tensile Modulus | 1mm/min | ISO 527 part 1/2 | 2800 | Mpa |
| Tensile Elongation | 50mm/min | ISO 527 part 1/2 | 8.0 | % |
| Flexural Modulus | ISO 178 | 2700 | Mpa | |
| Tensile Creep Modulus | 1 hour | ISO 899 part 1 | 2400 | Mpa |
| 1000 hours | ISO 899 part 1 | 1300 | Mpa | |
| Charpy Notched Impact Strength | 23℃ | ISO 179 1eA | 0.550 | J/cm² |
| 低温-30℃ | ISO 179 1eA | 0.550 | J/cm² | |
| Charpy Unnotched Impact Strength | 低温-30℃ | ISO 179 1eU | 12.0 | J/cm² |
| 23℃ | ISO 179 1eU | 12.0 | J/cm² | |
| Tensile Strength(Yield) | 50mm/min | ISO 527 part 1/2 | 63.0 | Mpa |
| Ball Indentation Hardness | 30sec数值 | ISO 2039 part 1 | 147 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Coefficient of Linear Thermal Expansion | 23-55℃ Longitudinal | ISO 11359 part 1/2 | 110 | µm/m-℃ |
| Deflection Temperature Under Load? | 1.8MPa | ISO 75 part 1/2 | 100 | °C |
| Melting Temperature | DSC,10 K/min | ISO 3146 method C1b | 166 | °C |
| Vicat Softening Temperature | VST/B/50 | ISO 306 | 150 | °C |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt index | 24.5cm3/10min,190℃/2.16kg | ISO 1133 | 34.55 | g/10min |
| Moisture Absorption | 23℃and50%RH | ISO 62 | 0.20 | % |
| Saturation23℃ | ISO 62 | 0.70 | % | |
| Density / Specific Gravity | ISO 1183 | 1.41 | g/cm³ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.