Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD | ISO294-4 | 1.5 | % |
Modeling Shrinkage | MD | ISO294-4 | 2.1 | % |
Melt Mass-Flow Rate | 190°C/2.16kg | ISO1133 | 1.3 | g/10min |
Density / Specific Gravity | | ISO1183 | 1.54 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Break | ISO527-2 | 53.0 | Mpa |
Tensile Strain | Break | ISO527-2 | 15 | % |
Tensile Modulus | | ISO527-2 | 2700 | Mpa |
Flexural Modulus | | ISO178 | 2500 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 87.0 | °C |
Linear thermal expansion coefficient | MD | ISO11359-2 | 1.1E-04 | cm/cm/°C |
Linear thermal expansion coefficient | TD | ISO11359-2 | 1.1E-04 | cm/cm/°C |
Melting Temperature | | ISO11357-3 | 178 | °C |
Annealing Temperature | | | 160 | °C |
Annealing Time-Optional | | | 30.0 | min/mm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Notched Impact Strength | 23°C | ISO179/1eA | 5.0 | kJ/m² |
Notched Izod Impact Strength | 23°C | ISO180/1A | 5.0 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 70 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 1.5mm | UL94 | HB | |
UL flame retardant rating | 3.0mm | UL94 | HB | |
UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | HB | |
UL flame retardant rating | 3.0mm | IEC60695-11-10,-20 | HB | |
FMVSS Flammability | | FMVSS302 | B | |
Burning Rate | 1.00mm | ISO3795 | <100 | mm/min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.