POM TENAC™ FS410 ASAHI JAPAN
128
- Unit Price:
- $5315 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 60MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High sliding wear resistant
- Application Areas:bearing
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.42 | ||
| Molding shrinkage rate | ASTM D955 | 1.8-2.2 | % | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 0.2 | % | |
| Melt index (flow coefficient) | ASTM D1238/ISO 1133 | 9 | g/10min |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | -，Flow | 旭化成法 | 1.8-2.2 | % |
| -，Across Flow | 旭化成法 | 1.8-2.2 | % | |
| Water absorption rate | ASTM D570 | 0.2 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Elongation rate | ASTM D638 | 30 | % | |
| IZOD notch impact strength | ASTM D256 | 39 | J/m | |
| tensile strength | ASTM D638/ISO 527 | 67 | kg/cm²(MPa)[Lb/in²] | |
| ASTM D638 | 67 | Mpa | ||
| Rockwell hardness | ASTM D785 | 94 | ||
| ASTM D785 | 94 | M | ||
| Bending modulus | ASTM D790 | 2940 | Mpa | |
| ASTM D790/ISO 178 | 2940 | kg/cm²(MPa)[Lb/in²] | ||
| bending strength | ASTM D790/ISO 178 | 98 | kg/cm²(MPa)[Lb/in²] | |
| ASTM D790 | 98 | Mpa | ||
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | 30 | % | |
| IZOD notch impact strength | ASTM D256/ISO 179 | 39 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame retardancy | UL94 | HB | ||
| Coefficient of linear expansion | TMA法 | 10 | ||
| Melt index | ASTM D1238 | 9 | g/10min | |
| Hot deformation temperature | ASTM D648/ISO 75 | 170 | ℃（℉） | |
| ASTM D648/ISO 75 | 136 | ℃（℉） | ||
| -，1.82MPa | ASTM D648 | 136 | °C | |
| -，0.45MPa | ASTM D648 | 170 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.