Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1.42 | |
Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.2 | % |
Melt Mass-Flow Rate | | ASTM D1238/ISO 1133 | 21 | g/10min |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | | 旭化成方法 | 1.7-2.1 | % |
Taber Abrasion Resistance | | ASTM D-1044 | 13 | mg/1000cycles |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Modulus | | ASTM D-790 | 2940 | Mpa |
Tensile Elongation | | ASTM D-638 | 45 | % |
Tensile Strength | | ASTM D-790 | 103 | Mpa |
Notched Izod Impact Strength | | ASTM D-256 | 59 | J/m |
Tensile Strength | | ASTM D638/ISO 527 | 69 | kg/cm²(MPa)[Lb/in²] |
Tensile Strength | | ASTM D-638 | 69 | Mpa |
Tensile Elongation | | ASTM D638/ISO 527 | 45 | % |
Rockwell Hardness | | ASTM D785 | 94 | |
Rockwell Hardness | | ASTM D-785 | 120 | R scale |
Rockwell Hardness | | ASTM D-785 | 94 | M Scale |
Flexural Modulus | | ASTM D790/ISO 178 | 2940 | kg/cm²(MPa)[Lb/in²] |
Flexural Strength | | ASTM D790/ISO 178 | 103 | kg/cm²(MPa)[Lb/in²] |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Burning Rate | | UL94 | HB | |
Deflection Temperature Under Load? | | ASTM D648/ISO 75 | 136 | ℃(℉) |
Deflection Temperature Under Load? | 0.45MPa | ASTM D-648 | 172 | °C |
Deflection Temperature Under Load? | 1.82MPa | ASTM D-648 | 136 | °C |
Linear expansion coefficient | | TMA | 10 | ×10-5cm/cm℃ |
Flammability | | UL 94 | HB | |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | | ASTM D-570 | 0.2 | % |
Melt index | | ASTM D-1238 | 21 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.