POM Iupital™ FU2025 MITSUBISHI ENGINEERING JAPAN
143
- Unit Price:
- $5590 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:wear resistant High mobility
- Application Areas:Electronic and Electrical Automotive sector
- Color:--
- Grade:Impact resistant grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density | ASTM D792/ISO 1183 | 1.35 | ||
| Modeling Shrinkage | ASTM D955 | 1.7 | % |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt index | ASTM D1238 | 6.0 | g/10min | |
| Modeling Shrinkage | Flow | 1.7 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Modulus | ASTM D638/ISO 527 | 1600 | kg/cm²(MPa)[Lb/in²] | |
| Tensile Strength | 23℃ | ASTM D638 | 34.3 | Mpa |
| Rockwell Hardness | ASTM D785 | 75 | M | |
| Flexural Modulus | ASTM D790/ISO 178 | 1400 | kg/cm²(MPa)[Lb/in²] | |
| 23℃ | ASTM D790 | 1.38 | GPa | |
| Flexural Strength | ASTM D790/ISO 178 | 48 | kg/cm²(MPa)[Lb/in²] | |
| 23℃ | ASTM D790 | 44.1 | Mpa | |
| Tensile Elongation | 23℃ | ASTM D638 | ＞300 | % |
| Izod Impact Strength | 3.2mm | ASTM D256 | 180 | J/m |
| Tensile Elongation?(Break) | ASTM D638/ISO 527 | >100 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning Rate | UL94 | HB | ||
| Deflection Temperature Under Load? | -，455Kpa | ASTM D648 | 147 | °C |
| -，820Kpa | ASTM D648 | 94 | °C | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | 1.2E-04 | mm/mm.℃ | |
| Flame retardancy | UL94 | HB |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface Resistivity | ASTM D257 | 1×10 | ||
| Volume Resistivity | ASTM D257 | 1×10 |
| Processing | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying conditions | 热风干燥 80℃---约3-4小时 | |||
| Screw Speed | 80-120 | rpm | ||
| Mold Temperature | ≦40 | °C | ||
| Processing temperature | 170 | °C | ||
| 190 | °C | |||
| 180 | °C | |||
| 180-210 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.