Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1.34 | |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
IZOD Notch Impact Strength | 3.20mm | J/m | ASTM D256 | 255 |
Tensile Elongation?(Break) | Break,23℃ | % | ISO 527-2 | |
Tensile Elongation?(Break) | Break,23℃ | % | ASTM D638 | 300 |
Tensile Strength | Yield,23℃ | MPa | ASTM D638 | |
Tensile Strength | Yield,23℃ | MPa | ISO 527-2 | |
Flexural Modulus | 23°C | MPa | ASTM D790 | 1340 |
Flexural Modulus | 23°C | MPa | ISO 178 | 1400 |
Flexural Modulus | | ASTM D790/ISO 178 | 181000 | kg/cm²(MPa)[Lb/in²] |
Flexural Strength | | ASTM D790/ISO 178 | 6670 | kg/cm²(MPa)[Lb/in²] |
Flexural Strength | 23°C | MPa | ISO 178 | 53.0 |
Flexural Strength | 23°C | MPa | ASTM D790 | 47.0 |
Charpy Notched Impact Strength | | kJ/m² | ISO 179/1eA | 18 |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Coefficient of Linear Thermal Expansion | flow,20 to 80°C | cm/cm/°C | ASTM D696 | 0.00013 |
Thermal distortion temperature | 1.8MPa,Unannealed | °C | ASTM D648 | 83.0 |
Thermal distortion temperature | 1.8MPa,Unannealed | °C | ISO 75-2/A | 72.0 |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | ohms | ASTM D257, IEC 60093 | |
Volume Resistivity | | ohm·cm | ASTM D257, IEC 60093 | |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Density | | g/cm³ | ASTM D792, ISO 1183 | |
Moisture Absorption | Equilibrium,23℃,60%rh | % | ASTM D570 | 0.24 |
Melt Mass-Flow Rate | 190℃/2.16kg | g/10 min | ASTM D1238 | 4.0 |
Melt Mass-Flow Rate | | g/10 min | ISO 1133 | 5.0 |
Other performance | Test Condition | Test Method | Test Result | Unit |
---|
Relative Temperature Index | 0.8mm | °C | UL 746 | 50.0 |
Relative Temperature Index | 0.8mm | °C | UL 746 | 50.0 |
Relative Temperature Index | 0.8mm | °C | UL 746 | 50.0 |
Flame Rating | 0.8mm | | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.