Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | //方向 | | 0.9 | % |
| Moisture Absorption | 23℃,60%RH | ASTM D-570 | 0.23 | % |
| Filler Content | | | High | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Strength(Break) | t2mm | ASTM D-732 | 670 | Kgf/cm |
| Tensile Elongation | 23℃ | ASTM D-638 | 4 | % |
| Flexural Strength | 23℃ | ASTM D-790 | 7.60 | |
| Tensile Impact Strength | t3.2mm S type | ASTM D-1822 | 55 | Kgf.cm/cm |
| Tensile Strength | 23℃ | ASTM D-638 | 900 | Kgf/cm |
| Rockwell Hardness | M scale | ASTM D-785 | M96 | |
| Flexural Strength | 23℃ | ASTM D-790 | 1430 | Kgf/cm |
| Izod Impact Strength | Notch t3.2mm | ASTM D-256 | 5.0 | Kgf.cm/cm |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flammability | t0.8mm | UL 94 | HB | |
| Coefficient of Linear Thermal Expansion | 20℃-80℃ | ASTM D-696 | 3.5 | |
| Deflection Temperature Under Load? | 18.6kgf/cm² | ASTM D-648 | 159 | °C |
| Deflection Temperature Under Load? | 4.6kgf/cm² | ASTM D-648 | 163 | °C |
| Melting Temperature | 10℃/min | DSC Method | 165 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface Resistivity | | ASTM D-257 | 1×10 | Ω |
| Volume Resistivity | | ASTM D-257 | 1×10 | Ω.cm |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | g/10 min | ASTM D-1238 | 15 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.