POM Delrin® 127UV DUPONT USA

Unit Price:
$6759 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
73MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High temperature resistan Flame retardant enhance
Application Areas:Medical supplies
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	TD	ISO294-4	1.9	%
Modeling Shrinkage	Modeling Shrinkage	MD	ISO294-4	2.1	%
Moisture Absorption	23°C,24hr	ISO62	0.50	%
	Moisture Absorption	Saturation,23°C,2.00mm	ISO62	1.2	%
	Moisture Absorption	Moisture Absorption	Equilibrium,23°C,2.00mm,50%RH	ISO62	0.30	%
Melt Mass-Flow Rate	190°C/2.16kg	ISO1133	2.4	g/10min
Melt Volume flow Rate	190°C/2.16kg	ISO1133	1.90	cm3/10min
Density / Specific Gravity		ISO1183	1.42	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Nominal Tensile Strain at Break		ISO527-2	45	%
Tensile Stress	Yield	ISO527-2	70.0	Mpa
Tensile Strain	Yield	ISO527-2	23	%
Tensile Modulus		ISO527-2	3000	Mpa
Flexural Modulus		ISO178	2700	Mpa
Flexural Stress	3.5%Strain	ISO178	80.5	Mpa
Flexural Stress	Flexural Stress	--	ISO178	72.0	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Linear thermal expansion coefficient	MD	ISO11359-2	1.2E-04	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD	ISO11359-2	1.1E-04	cm/cm/°C
Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	160	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	93.0	°C
Vicat Softening Temperature		ISO306/B50	160	°C
Melting Temperature		ISO11357-3	178	°C
Annealing Temperature			160	°C
Annealing Time-Optional			30.0	min/mm

Electrical performance	Test Condition	Test Method	Test Result	Unit
Relative Permittivity	100Hz	IEC60250	3.50
Relative Permittivity	Relative Permittivity	1MHz	IEC60250	3.40
Comparative Tracking Index		IEC60112	600	V
Volume Resistivity		IEC60093	1E+13	ohms·cm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	350	kJ/m²
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	400	kJ/m²
Charpy Notched Impact Strength	-30°C	ISO179/1eA	11	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	15	kJ/m²
Notched Izod Impact Strength	-40°C	ISO180/1A	11	kJ/m²
Notched Izod Impact Strength	Notched Izod Impact Strength	23°C	ISO180/1A	13	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	M-Sale	ISO2039-2	92
Rockwell Hardness	Rockwell Hardness	R-Sale	ISO2039-2	120

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.8mm	UL94	HB
UL flame retardant rating	UL flame retardant rating	0.8mm	IEC60695-11-10,-20	HB
FMVSS Flammability		FMVSS302	B
Fogging-G-value	condensate	ISO6452	1.5E-04	g
Burning Rate	1.00mm	ISO3795	28	mm/min

Supplementary information	Test Method	Test Result	Unit
Emission	VDA275	<8.00	mg/kg
EmissionofOrganicCompounds	VDA277	16.0	µgC/g
Odor	VDA270	3.00

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.