Material Description

Technical Data Sheet

Material Description

Material Properties:wear resistant High rigidity high strength enhance High impact resistance High mobility
Application Areas:Thin walled products Fiber grade
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	Saturation,23°C,2.00mm	ISO62	1.4	%
Moisture Absorption	Moisture Absorption	Equilibrium,23°C,2.00mm,50%RH	ISO62	0.40	%
Modeling Shrinkage	TD	ISO294-4	1.9	%
Modeling Shrinkage	Modeling Shrinkage	MD	ISO294-4	1.9	%
Melt Mass-Flow Rate		ISO1133	25	g/10min
Melt Volume flow Rate	190°C/2.16kg	ISO1133	21.0	cm3/10min
Density / Specific Gravity		ISO1183	1.42	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
CoefficientFriction	vs.Itself-Dynamic,1hr	ASTMD1894	0.25
Nominal Tensile Strain at Break		ISO527-2	23	%
Tensile Creep Modulus	1000hr	ISO899-1	1500	Mpa
Tensile Creep Modulus	1hr	ISO899-1	2800	Mpa
Tensile Stress	Yield	ISO527-2	71.0	Mpa
Tensile Strain	Yield	ISO527-2	12	%
Tensile Modulus		ISO527-2	3300	Mpa
Flexural Modulus		ISO178	3000	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	162	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	94.0	°C
Linear thermal expansion coefficient	MD：23to55°C	ASTME831	1E-04	cm/cm/°C
	Linear thermal expansion coefficient	MD	ISO11359-2	1.2E-04	cm/cm/°C
	Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD	ISO11359-2	1.2E-04	cm/cm/°C
Vicat Softening Temperature		ISO306/B50	160	°C
Melting Temperature		ISO11357-3	178	°C
Annealing Temperature			160	°C
Annealing Time-Optional			30.0	min/mm
Effective Thermal Diffusivity			8E-08	m²/s

Electrical performance	Test Condition	Test Method	Test Result	Unit
Relative Permittivity	100Hz	IEC60250	3.80
Relative Permittivity	Relative Permittivity	1MHz	IEC60250	3.80
Comparative Tracking Index		IEC60112	600	V
Surface Resistivity		IEC60093	>1.0E+15	ohms
Volume Resistivity		IEC60093	1E+14	ohms·cm
Hot-wireIgnition	0.750mm	UL746	8.0	sec

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	-30°C	ISO179/1eA	7.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	8.0	kJ/m²
Notched Izod Impact Strength	23°C	ISO180/1A	7.0	kJ/m²
Notched Izod Impact Strength	Notched Izod Impact Strength	-40°C	ISO180/1A	8.0	kJ/m²
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	200	kJ/m²
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	200	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	M-Sale	ISO2039-2	92
Rockwell Hardness	Rockwell Hardness	R-Sale	ISO2039-2	120

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.8mm	UL94	HB
	UL flame retardant rating	1.5mm	UL94	HB
		UL flame retardant rating	0.8mm	IEC60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	1.5mm	IEC60695-11-10,-20	HB
Oxygen Index		ISO4589-2	23	%
FMVSS Flammability		FMVSS302	B
atomization	F-value(refraction)	ISO6452	95	%
atomization	atomization	G-value(condensate)	ISO6452	2E-04	g
Burning Rate	1.00mm	ISO3795	20	mm/min

Supplementary information	Test Condition	Test Method	Test Result	Unit
Emission		VDA275	<8.00	mg/kg
EmissionofOrganicCompounds		VDA277	4.30	µgC/g

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.