LLDPE ML2202 SINOPEC SHANGHAI
41
- Unit Price:
- $1323 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 54MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Viscosity | ISO 1003 | 65 | % | |
Gloss | ISO 2457 | 15 | % | |
Melting temperature | ISO3146 | 124 | °C |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Film Puncture Force | 北欧化工 | 5 | J | |
Film Puncture Force | 北欧化工 | 60 | N | |
Instrumented Dart Impact | ISO 7765-1A | 300 | g | |
Tensile Strength(Yield) | Across Flow | ISO 527-3 | - | Mpa |
Across Flow | ISO 527-3 | 13 | Mpa | |
Tensile Elongation?(Break) | Across Flow | ISO 527-3 | 600 | % |
Across Flow | ISO 527-3 | 900 | % | |
Tensile Modulus | Across Flow | ISO 527-3 | 250 | Mpa |
Across Flow | ISO 527-3 | 300 | Mpa | |
Tensile Strength | Across Flow | ISO 527-3 | 50 | Mpa |
Across Flow | ISO 527-3 | 35 | Mpa | |
Tearing Strength | Across Flow | ISO 527-3 | 3 | N |
Across Flow | ISO 527-3 | 7 | N |
Other | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
热粘力 | 北欧化工 | 2.5 | N |
Physical | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Melt index | 190℃,2.16kg | ISO 1133 | 0.25 | g/10min |
190℃,5kg | ISO 1133 | 1.0 | g/10min | |
190℃,21.6kg | ISO 1133 | 22 | g/10min | |
Density | ISO 1183 | 923 | kg/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.