LLDPE Lotrène® Q2018C QATAR PETROCHEMICAL
85
- Unit Price:
- $1413 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Mass-Flow Rate | 190°C/2.16kg | ASTMD1238 | 2.0 | g/10min |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat Softening Temperature | ASTMD15253 | 100 | °C | |
| Melting temperature | 内部方法 | 121 | °C |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Film Thickness - Tested) | 20 | µm | ||
| Tensile Modulus | 1%Secant,MD:20μm,铸造薄膜 | ISO178 | 165 | Mpa |
| 1%Secant,TD:20μm,铸造薄膜 | ISO178 | 170 | Mpa | |
| Tensile Stress | MD:Yield,20μm,挤塑薄膜 | ISO527-3 | 9.70 | Mpa |
| TD:Yield,20μm,挤塑薄膜 | ISO527-3 | 9.60 | Mpa | |
| MD:Break,20μm,挤塑薄膜 | ISO527-3 | 37.0 | Mpa | |
| TD:Break,20μm,挤塑薄膜 | ISO527-3 | 23.0 | Mpa | |
| Tensile Elongation | MD:Break,20μm,挤塑薄膜 | ISO527-3 | 330 | % |
| TD:Break,20μm,挤塑薄膜 | ISO527-3 | 670 | % | |
| Elmendorf Tear Strength | MD:20µm,铸造薄膜 | ISO6383-2 | 12 | N |
| TD:20µm,铸造薄膜 | ISO6383-2 | 190 | N | |
| DartDropImpact2 | 20µm,CastFilm | ISO7765-1 | 35 | g |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Haze | 20.0µm,铸造薄膜 | ISO14782 | 1.8 | % |
| Gloss | 45°,20.0µm,铸造薄膜 | ASTMD2457 | 92 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.