Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 0.918 | |
Melt Mass-Flow Rate | | ASTM D1238/ISO 1133 | 2.0 | g/10min |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 190°C/2.16kg | ASTMD1238 | 2.0 | g/10min |
Film | Test Condition | Test Method | Test Result | Unit |
---|
Film Thickness - Tested) | | | 25 | µm |
Tensile Strain (MD) | Break,25µm,BlownFilm | ASTMD882 | 660 | % |
Tensile Strength (MD) | Break,25µm,BlownFilm | ASTMD882 | 32.0 | Mpa |
Tensile Strength (MD) | Yield,25µm,BlownFilm | ASTMD882 | 10.0 | Mpa |
Tensile Strength (TD) | Yield,25µm,BlownFilm | ASTMD882 | 10.0 | Mpa |
Tensile Strength (TD) | Break,25µm,BlownFilm | ASTMD882 | 25.0 | Mpa |
Tensile Strain (TD) | Break,25µm,BlownFilm | ASTMD882 | 700 | % |
Elmendorf Tear Strength (TD) | 25µm,BlownFilm | ASTMD1922 | 330 | g |
Gardner Impact | 25μm,Blown Film | ASTMD1709A | 100 | g |
Elmendorf Tear Strength (MD) | 25µm,BlownFilm | ASTMD1922 | 110 | g |
Secant Modulus (1%Secant,MD) | 25µm,BlownFilm | ASTMD882 | 170 | Mpa |
Secant Modulus (1%Secant,TD) | 25µm,BlownFilm | ASTMD882 | 190 | Mpa |
optical performance | Test Condition | Test Method | Test Result | Unit |
---|
Gloss | 45°,25.0μm,Blown Film | ASTMD2457 | 43 | |
Haze | 25.0μm,Blown Film | ASTMD1003 | 14 | % |
Supplementary information | Test Condition | Test Method | Test Result | Unit |
---|
LowFrictionPuncture-BlownFilm | 25.0µm | 内部方法 | 290 | J/cm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.