Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 190°C/2.16kg | ASTMD1238 | 1.2 | g/10min |
| Density / Specific Gravity | | ASTMD1505 | 0.919 | g/cm³ |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | | ASTMD1525 | 102 | °C |
| Brittleness Temperature | | ASTMD746 | <-70.0 | °C |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|
| Film Thickness - Tested) | | ASTMD746 | 50 | µm |
| Spencer | 50.0µm | ASTMD3420 | 0.981 | J |
| Tensile Elongation | MD:Break,50μm | ASTMD882 | 750 | % |
| Tensile Elongation | TD:Break,50μm | ASTMD882 | 850 | % |
| Tensile Strength | TD:Break,50μm | ASTMD882 | 35.3 | Mpa |
| Tensile Strength | MD:Yield,50μm | ASTMD882 | 11.8 | Mpa |
| Tensile Strength | TD:Yield,50μm | ASTMD882 | 10.8 | Mpa |
| Tensile Strength | MD:Break,50μm | ASTMD882 | 42.2 | Mpa |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Haze | | ASTMD1003 | 20 | % |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|
| Tearing Strength | MD:50.0µm | ASTMD1922 | 49.0 | kN/m |
| Tearing Strength | TD:50.0µm | ASTMD1922 | 117.7 | kN/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.