LDPE ATTANE™ 4203 STYRON US
139
- Unit Price:
- $1854 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 49MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low temperature resistanc High impact resistance Compliant with Canadian H Excellent elasticity and Resistance to cracking an
- Application Areas:packing film container Used for packaging
- Color:--
- Grade:Thin film grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 190°C/2.16kg | ASTMD1238 | 0.80 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| elongation at break | 20μm (MD) | ASTM D882 | 445 | % |
| tensile strength | 20 μm (MD) | ASTM D882 | 53 | Mpa |
| Tensile yield strength | ASTM D882 | 9 | Mpa | |
| Puncture intensity | (20 μm) | 陶氏企业测试 | 22 | J/cm |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melting temperature (DSC) | 内部方法 | 123 | °C | |
| vicat softening point | ASTM D1525 | 84 | °C | |
| Vicat softening temperature | ASTMD1525 | 83.9 | °C |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Membrane puncture strength | 内部方法 | 4.52 | J | |
| Membrane piercing force | 内部方法 | 48.9 | N | |
| Membrane strength | MD | ASTMD882 | 45.5 | J/cm³ |
| TD | ASTMD882 | 64.5 | J/cm³ | |
| Film thickness - tested | 25 | µm | ||
| Secant modulus | 1%Secant,MD | ASTMD882 | 98.6 | Mpa |
| 2%Secant,MD | ASTMD882 | 89.6 | Mpa | |
| 1%Secant,TD | ASTMD882 | 113 | Mpa | |
| 2%Secant,TD | ASTMD882 | 93.8 | Mpa | |
| elongation | MD:Break | ASTMD882 | 340 | % |
| TD:Break | ASTMD882 | 570 | % | |
| Elmondov tear strength | MD | ASTMD1922 | 370 | g |
| TD | ASTMD1922 | 520 | g | |
| Tensile strength | MD:Yield | ASTMD882 | 6.21 | Mpa |
| TD:Yield | ASTMD882 | 5.86 | Mpa | |
| MD:Break | ASTMD882 | 32.4 | Mpa | |
| TD:Break | ASTMD882 | 30.0 | Mpa | |
| Falling hammer impact | ASTMD1709B | >1100 | g | |
| Membrane puncture resistance | 内部方法 | 24.8 | J/cm³ |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Sealing starting temperature | 陶氏企业测试 | 88 | °C |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| transparency | 20μm | ASTM D1746 | 93 | |
| gloss | 45° | ASTMD2457 | 39 | |
| 20 μm | ASTM D2457 | 48 | ||
| Haze | ASTMD1003 | 14 | % | |
| ASTM D1003 | 5 | % |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt index | ASTM D1238 | 0.8 | g/10min | |
| density | ASTM D792 | 0.905 | g/cm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.