LDPE COSMOTHENE® G814 TPC SINGAPORE

Unit Price:
$2254 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
10.5MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Method	Test Result	Unit
Density	ASTM D792/ISO 1183	0.917
Modeling Shrinkage	ASTM D955	3.0	%
Moisture Absorption 23℃/24H	ASTM D570/ISO 62	0.002	%
Melt Mass-Flow Rate	ASTM D1238/ISO 1133	50	g/10min

Physical Properties	Test Condition	Test Method	Test Result	Unit
Melt Mass-Flow Rate		ASTMD1238	50	g/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Strength(Break)		D-638	95	kg/cm
Tensile Strength	Break	ASTMD638	9.32	Mpa
Tensile Elongation?(Break)		ASTM D638/ISO 527	500	%
Tensile Strength		ASTM D638/ISO 527	95	kg/cm²(MPa)[Lb/in²]
Tensile Elongation		ASTM D638/ISO 527	500	%
	Tensile Elongation		D-638	500	%
	Tensile Elongation	Tensile Elongation	Break	ASTMD638	500	%
Rockwell Hardness		ASTM D785	65
Flexural Strength		D-747	1800	kg/cm
Flexural Modulus		ASTMD747	157	Mpa
Tensile Elongation?(Break)		ASTM D638/ISO 527	480	%

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?		ASTM D648/ISO 75	78	℃（℉）
Melting temperature			105	°C

Processing	Test Condition	Test Method	Test Result	Unit
Processing temperature			230	°C
	Processing temperature			210	°C
		Processing temperature			220	°C
		Processing temperature	Processing temperature			190	°C
Screw Speed			2800	rpm
Melt Temperature			106	°C
Mold Temperature			70	°C

Physical	Test Condition	Test Method	Test Result	Unit
Density		D-1505	0.917	g/cm

Other performance	Test Condition	Test Method	Test Result	Unit
Melt index		D-1238	50	g/10min
Melting Temperature		TPC	106	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.