Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 190°C/2.16kg | ISO1133 | 0.20 | g/10min |
| Melt Mass-Flow Rate | 190°C/21.6kg | ISO1133 | 20 | g/10min |
| Melt Mass-Flow Rate | 190°C/5.0kg | ISO1133 | 0.90 | g/10min |
| Density / Specific Gravity | | ISO1183 | 0.931 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Coefficient of Friction | Itself - Dynamic,Blown Film | ISO8295 | 0.40 | |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melting temperature | | ISO11357-3 | 127 | °C |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|
| Film Thickness - Tested) | | | 40 | µm |
| Tensile Modulus | MD:40μm,Blown Film | ISO527-3 | 300 | Mpa |
| Tensile Modulus | TD:40μm,Blown Film | ISO527-3 | 400 | Mpa |
| Tensile Elongation | MD:Break,40μm,Blown Film | ISO527-3 | 400 | % |
| Tensile Elongation | TD:Break,40μm,Blown Film | ISO527-3 | 700 | % |
| Tensile Strength | MD:40μm,Blown Film | ISO527-3 | 50.0 | Mpa |
| Tensile Strength | TD:40μm,Blown Film | ISO527-3 | 40.0 | Mpa |
| Gardner Impact | 40μm,Blown Film | ISO7765-1 | 230 | g |
| ElmendorfTearStrength | MD:40.0µm1 | ISO6383-2 | 50.0 | kN/m |
| ElmendorfTearStrength | TD:40.0µm2 | ISO6383-2 | 250.0 | kN/m |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| 仪器化投掷冲击-TotalPenetrationEnergy3 | 40.0µm | ISO7765-2 | 200 | J/cm |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Haze | 40.0μm,Blown Film | ASTMD1003 | 80 | % |
| Gloss | 40.0μm,Blown Film | ASTMD2457 | 7 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.