HDPE UNIVL™ DMDD-6200 DOW JAPAN

Unit Price:
$1249 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Environmental Stress Cracking Resistance	50°C,100%Igepal,F50	ASTMD1693	50.0	hr
Melt Mass-Flow Rate	190°C/2.16kg	ASTMD1238	0.25	g/10min
Melt Mass-Flow Rate	Melt Mass-Flow Rate	190°C/21.6kg	ASTMD1238	23	g/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Strength(Break)		ASTM D-638	25.5	Mpa
Flexural Modulus (2% Secant)		ASTMD790B	1020	Mpa
Flexural Modulus (2% Secant)		ASTM D-790B	1020	Mpa
Shore Hardness	Shore D	ASTM D-2240	59
Tensile Elongation?(Yield)		ASTM D-638	6	%
Environmental Stress Cracking Resistance	50℃，10% Igepal，F50	ASTM D-1693	50	hr
Tensile Strength		ASTM D-1822	210	KJ/m
Tensile Strength(Yield)		ASTM D-638	26.2	Mpa
Tensile Elongation?(Break)		ASTM D-638	900	%
Tensile Elongation	Yield	ASTMD638	6.0	%
Tensile Elongation	Tensile Elongation	Break	ASTMD638	900	%
Tensile Strength	Yield	ASTMD638	26.2	Mpa
Tensile Strength	Tensile Strength	Break	ASTMD638	25.5	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature		ASTMD1525	129	°C
Deflection Temperature Under Load?	0.45MPa,Unannealed	ASTMD648	70.0	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	0.45MPa，Unannealed	ASTM D-648	70	°C
Vicat Softening Temperature		ASTM D-1525	129	°C
Brittleness Temperature		ASTM D-746		°C
Brittleness Temperature	Brittleness Temperature		ASTMD746	<-76.1	°C
Melting temperature (DSC)		内部方法	132	°C
Melting temperature		Internal Method	132	°C
Peak Crystallization Temperature		Internal Method	119	°C
Peak Crystallization Temperature?	DSC	内部方法	119	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Tensile Impact Strength		ASTMD1822	210	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Shore Hardness	Shore D	ASTMD2240	59

Physical	Test Condition	Test Method	Test Result	Unit
Melt index	190℃/2.16kg	ASTM D-1238	0.25	g/10min
Melt index	Melt index	190℃/21.6kg	ASTM D-1238	23	g/10min
Density		ASTM D-792	0.953	g/cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.