HDPE Borstar® FB1520 BOREALIS EUROPE

Unit Price:
$1534 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
40MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Density		ASTM D792/ISO 1183	0.952
Melt Mass-Flow Rate		ASTM D1238/ISO 1133	<0.25	g/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Strength(Yield)	15.0µm	ASTM D-882	35	Mpa
Environmental Stress Cracking Resistance	10% Igepal，F50	ASTM D-1693	＞1000	hr
Tensile Elongation (Break MD)	15.0µm	ASTM D-882	350	%
Tensile Elongation (Break TD)	15.0µm	ASTM D-882	450
Elmendorf Tear Strength (TD)	15.0µm	ASTM D-1922	40	g
Elmendorf Tear Strength (MD)	15.0µm	ASTM D-1922	20
Secant Modulus (MD)	15.0µm	ASTM D-882	750	Mpa
Secant Modulus (TD)	15.0µm	ASTM D-882	900
Tensile Strength (Break TD)	15.0µm	ASTM D-882	95
Tensile Strength (Break TD)	15.0µm	ASTM D-882	100

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Melting temperature		ISO 11357-3	133	°C
Melting Temperature			271 F	℃（℉）
Vicat Softening Temperature		ASTM D1525/ISO R306	264 F	℃（℉）
Vicat Softening Temperature	Vicat Softening Temperature		ISO 306	129	°C
Melt Temperature			210-230	°C

Physical	Test Condition	Test Method	Test Result	Unit
Density		ASTM D-1505	0.952	g/m3
Melt Mass-Flow Rate	190℃/2.16 kg	ASTM D-1238	＜0.10	g/10min
	Melt Mass-Flow Rate	190℃/21.6kg	ASTM D-1238	7	g/10min
	Melt Mass-Flow Rate	Melt Mass-Flow Rate	190℃/5.0kg	ASTM D-1238	0.25	g/10min

Other performance	Test Condition	Test Method	Test Result	Unit
Film Puncture Force	15.0µm	ASTM D-5748	0.7	J
Film Puncture Force	15.0µm	ASTM D-5748	30	N
Film Thickness			15	µm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.