HDPE SABIC® F01552 SABIC SAUDI
98
- Unit Price:
- $1858 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:film Bag
- Color:--
- Grade:Thin film grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Mass-Flow Rate | 190°C/2.16 kg | ISO 1133 | 0.15 | g/10 min |
| 190°C/21.6 kg | ISO 1133 | 16 | g/10 min | |
| Density | ASTM D1505 | 0.952 | g/cm³ |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat Softening Temperature | ASTM D1525 | 125 | °C |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Elongation | MD : Break, 15 μm, Blown Film 1 | ASTM D882 | 400 | % |
| TD : Break, 15 μm, Blown Film 2 | ASTM D882 | 610 | % | |
| Elmendorf Tear Strength | MD | ASTM D1922 | 4.0 | g |
| TD | ASTM D1922 | 40 | g | |
| Gardner Impact | ASTM D1709 | 180 | g | |
| Secant Modulus | 1% Secant, MD : 15 μm, Blown Film | ASTM D882 | 1400 | Mpa |
| 1% Secant, TD : 15 μm, Blown Film | ASTM D882 | 1700 | Mpa | |
| Tensile Strength | MD : Yield, 15 μm, Blown Film | ASTM D882 | 31.0 | Mpa |
| TD : Yield, 15 μm, Blown Film | ASTM D882 | 30.0 | Mpa | |
| MD : Break, 15 μm, Blown Film | ASTM D882 | 55.0 | Mpa | |
| TD : Break, 15 μm, Blown Film | ASTM D882 | 49.0 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.