Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | | ISO 294-4 | 0.20 到 0.60 | % |
Moisture Absorption | Equilibrium, 23°C, 50% RH | ISO 62 | 0.30 | % |
Melt Mass-Flow Rate | 230°C/3.8 kg | ISO 1133 | 3.5 | g/10 min |
Melt Volume flow Rate | 230°C/3.8 kg | ISO 1133 | 3.40 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Stress | | ISO 178/A | 95.0 | Mpa |
Tensile Modulus | | ISO 527-2/1A/1 | 3300 | Mpa |
Flexural Modulus | | ISO 178/A | 3200 | Mpa |
Tensile Stress | Yield | ISO 527-2/1A/5 | 70.0 | Mpa |
Tensile Stress | Break | ISO 527-2/1A/5 | 70.0 | Mpa |
Tensile Strain | Yield | ISO 527-2/1A/5 | 5.0 | % |
Tensile Strain | Break | ISO 527-2/1A/5 | 5.0 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45 MPa, Annealed | ISO 75-2/B | 104 | °C |
Deflection Temperature Under Load? | 1.8 MPa, Annealed | ISO 75-2/A | 99.0 | °C |
Vicat Softening Temperature | -- | ISO 306/A50 | 113 | °C |
Vicat Softening Temperature | -- | ISO 306/B50 | 106 | °C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | | ISO 179/1eU | 20 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | M -Sale | ISO 2039-2 | 97 | |
optical performance | Test Condition | Test Method | Test Result | Unit |
---|
Index of Refraction | | ISO 489 | 1.490 | |
Transmittance | 3180 µm | ASTM D1003 | 92.0 | % |
Haze | 3180 µm | ASTM D1003 | < 1.0 | % |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | | UL 94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.