Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt index | 230℃/3.8 kg | ISO 1133 | 1.8 | g/10 min |
Modeling Shrinkage | | | 0.002-0.006 | % |
Modeling Shrinkage | | Internal Method | 0.20-0.60 | % |
Moisture Absorption | 23℃ | ISO 62 | 0.30 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Break | ISO 527-2/1A/5 | 77 | Mpa |
Tensile Strain | Break | ISO 527-2/1A/5 | 6.0 | % |
Flexural Modulus | | | 3400 | Mpa |
Impact Strength | 悬臂梁V型Notched | | 0.016 | KJ/m |
Charpy Notched Impact Strength | | ISO 179/1eA | 1.4 | kJ/m² |
Charpy Notched Impact Strength | | ISO 179/1eU | 22 | kJ/m² |
Tensile Modulus | | ISO 527-2/1A/1 | 3300 | |
Tensile Strength | | | 74.0 | Mpa |
Tensile Elongation | Break | | 5 | % |
Rockwell Hardness | | ISO 2039-2 | 100 | |
Rockwell Hardness | | | 100 | M标度 |
Flexural Modulus | | ISO 178 | 3300 | Mpa |
Flexural Strength | | ISO 178 | 130 | Mpa |
Flexural Strength | | | 120.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 经Annealed | | 100 | °C |
Deflection Temperature Under Load? | | ISO 75-2/A | 100 | °C |
Vicat Softening Temperature | | ISO 306/B50 | 109 | °C |
optical performance | Test Condition | Test Method | Test Result | Unit |
---|
Light Transmittance | | | 93 | % |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | | ASTM D570 | 0.3 | % |
Melt index | 条件I | ASTM D1238 | 2 | g/10min |
Melt index | 条件L | | 0.9 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.