Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Refractive index of light | | ASTM D-542 | 1.49 | |
| Transmittance | 2mm | ASTM D-1003 | 93 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Elongation | | ASTM D-638 | 7 | % |
| tensile strength | | ASTM D-638 | 69[700] | MPa[KG/cm |
| Flexural Strength | 1/4"棒 | ASTM D-790 | 103[1050] | MPa[KG/cm |
| Notched Izod Impact Strength | 1/4槽口副 | ASTM D-256 | 16[1.6] | J/m[kg.cm/cm] |
| Rockwell Hardness | | ASTM D-785 | 92 | M Scale |
| Flexural Modulus | 1/4"棒 | ASTM D-790 | 3.0[3.1×10 | GPa[KG/cm |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | 9.8N | ASTM D-1525 | 104 | °C |
| Specific Heat | | JIS K-7123 | 1.5[0.35] | J/g.c[(cal/g/℃)] |
| Coefficient of thermal expansion | | ASTM D-177 | 0.2 | W/m℃ |
| Coefficient of Linear Thermal Expansion | | ASTM D-696 | 6×10 | 1/℃ |
| Heat Deflection Temperature | 1.82MPa | ASTM D-648 | 89 | °C |
| Spiral Flow | 230℃ | MRC | 190-290 | mm |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume Resistivity | | JIS K-6911 | ＞10 | m[cm] |
| Dissipation Factor?(Tangent) | 60Hz | | 0.05 | |
| Insulation Resistance | | | 20[20] | MV/m[KV/mm] |
| Dielectric Constant | 60Hz | | 3.7 | |
| Arc Resistance | | JIS K-6911 | 没有痕迹 | |
| Surface Resistivity | | JIS K-6911 | ＞10 | |
| Processing | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | | ASTM D-955 | 0.2-0.5 | % |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | 24hr | ASTM D-570 | 0.3 | % |
| Melt index | 230℃，37.3n | ASTM D-1238 | 6.0 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.