Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | | 内部方法 | 0.30到0.70 | % |
Modeling Shrinkage | | | 0.003-0.007 | cm/cm |
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.30 | % |
Melt Mass-Flow Rate | 230°C/3.8kg | ISO1133 | 1.3 | g/10min |
Transmittance | | | 92-93 | % |
SpiralFlow3,4 | | 内部方法 | 25.0 | CM |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Modulus | | | 2500 | Mpa |
Notched Izod Impact Strength | | | 2.5 | KJ/m |
Refractive index of light | | | 1.49 | |
Flexural Strength | | | 90 | Mpa |
Tensile Stress | Break | ISO527-2/1A/5 | 60.0 | Mpa |
Tensile Strain | Break | ISO527-2/1A/5 | 20 | % |
Flexural Stress | | ISO178 | 100 | Mpa |
Tensile Modulus | | ISO527-2/1A/1 | 2400 | Mpa |
Tensile Strength | | | 56 | Mpa |
Tensile Elongation | | | 20 | % |
Rockwell Hardness | | | 118 | M-scale/R-scale |
Flexural Modulus | | ISO178 | 2400 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | | | 96 | °C |
Deflection Temperature Under Load? | | ISO75-2 | 94 | °C |
Vicat Softening Temperature | | ISO306/B50 | 102 | °C |
Coefficient of Linear Thermal Expansion | | | 8×10 | cm/cm.℃ |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | | ISO179/1eU | 25 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R-Sale | ISO2039-2 | 118 | |
optical performance | Test Condition | Test Method | Test Result | Unit |
---|
Transmittance | Total | ISO13468-1 | 92.0 | % |
Refractive index of light | | ISO489 | 1.490 | |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Melt index | | | 1.0 | g/10min |
Moisture Absorption | | | 0.3 | % |
UL | | | 94HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.