Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Density		ASTM D792/ISO 1183	1.16
Melt Mass-Flow Rate		ASTM D1238/ISO 1133	1.8	g/10min

Physical Properties	Test Condition	Test Method	Test Result	Unit
Melt index	230℃/3.8 kg	ASTM D1238	1.8	g/10 min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Strength	Yield, 3.18 mm	ASTM D638	70.3	Mpa
Notched Izod Impact Strength	23℃, 6.35 mm	ASTM D256	20	J/m
Tensile Elongation?(Break)		ASTM D638/ISO 527	5.0	%
Tensile Strength		ASTM D638/ISO 527	70.3	kg/cm²(MPa)[Lb/in²]
Tensile Elongation	Break, 3.18 mm	ASTM D638	5.0	%
Rockwell Hardness	M -Sale, 6.35 mm	ASTM D785	95
Rockwell Hardness	Rockwell Hardness		ASTM D785	95
Flexural Strength		ASTM D790/ISO 178	108	kg/cm²(MPa)[Lb/in²]
Flexural Strength	Flexural Strength	6.35 mm	ASTM D790	108	Mpa
Izod notch impact strength		ASTM D256/ISO 179	20	kg·cm/cm(J/M)ft·lb/in

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?		ASTM D648/ISO 75	100	℃（℉）
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 6.35 mm	ASTM D648	100	°C
Vicat Softening Temperature		ASTM D1525/ISO R306	113	℃（℉）
Vicat Softening Temperature		ASTM D1525	113	°C
Flame Rating	1.59 mm	UL 94	HB

Electrical performance	Test Condition	Test Method	Test Result	Unit
Transmittance	3180 µm	ASTM D1003	91.0	%
Haze	3.18 µm	ASTM D1003	< 1.0	%
The Yellow Index	3.18 mm	ASTM D1003	0.50 到 1.0	YI

optical performance	Test Condition	Test Method	Test Result	Unit
Transmittance		ASTM D1003/ISO 13468	91.0	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.