Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1.19 | |
Modeling Shrinkage | | ASTM D955 | 0.002-0.006 | % |
Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.3 | % |
Melt Mass-Flow Rate | | ASTM D1238/ISO 1133 | 8 | g/10min |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt index | 230℃/3.8 kg | ISO 1133 | 8.0 | g/10 min |
Modeling Shrinkage | | Internal Method | 0.20-0.60 | % |
Moisture Absorption | Saturation, 23℃ | ISO 62 | 0.30 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Break | ISO 527-2/1A/5 | 72.0 | Mpa |
Tensile Strain | Break | ISO 527-2/1A/5 | 5.0 | % |
Charpy Notched Impact Strength | | ISO 179/1eU | 20 | kJ/m² |
Charpy Notched Impact Strength | | ISO 179/1eA | 1.3 | kJ/m² |
Tensile Modulus | | ISO 527-2/1A/1 | 3200 | |
Tensile Strength | | ASTM D638/ISO 527 | 71 | kg/cm²(MPa)[Lb/in²] |
Tensile Elongation | | ASTM D638/ISO 527 | 5 | % |
Rockwell Hardness | | ASTM D785 | M95 | |
Flexural Modulus | | ASTM D790/ISO 178 | 3300 | kg/cm²(MPa)[Lb/in²] |
Flexural Modulus | | ISO 178 | 3200 | Mpa |
Flexural Strength | | ISO 178 | 120 | Mpa |
Flexural Strength | | ASTM D790/ISO 178 | 110 | kg/cm²(MPa)[Lb/in²] |
Izod notch impact strength | | ASTM D256/ISO 179 | 1.6 | kg·cm/cm(J/M)ft·lb/in |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | | ASTM D648/ISO 75 | 89 | ℃(℉) |
Deflection Temperature Under Load? | 1.8 MPa, Unannealed | ISO 75-2/A | 91 | °C |
Vicat Softening Temperature | | ISO 306/B50 | 98 | °C |
optical performance | Test Condition | Test Method | Test Result | Unit |
---|
Transmittance | | ASTM D1003/ISO 13468 | 93 | % |
Refractive index of light | | ASTM D542/ISO 489 | 1.49 | |
Other performance | Test Condition | Test Method | Test Result | Unit |
---|
Refractive index of light | | ISO 489 | 1.490 | |
Transmittance | Total | ISO 13468-1 | 92.0 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.