Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Haze | 3mm | ISO 14782 | 0.3 | % |
Refractive index of light | Nd | ISO 489 | 1.49 | |
Light Transmittance | 3mm | ISO 13468-1 | 93 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod Impact Strength | 1A | JIS K7110 | 1.6 | KJ/m |
tensile strength | 1A/5 | ISO 527-2 | 62 | Mpa |
Tensile Elongation | 1A/1 | ISO 527-2 | 3.3 | GPa |
Flexural Strength | | ISO 178 | 92 | Mpa |
Notched Izod Impact Strength | 1eU 无槽口 | JIS K7111 | 21 | KJ/m |
Notched Izod Impact Strength | 1eA V槽口 | JIS K7111 | 1.2 | KJ/m |
Tensile Elongation | 1A/5 | ISO 527-2 | 5 | % |
Rockwell Hardness | M scale | ISO 2039 | 101 | |
Flexural Modulus | | ISO 178 | 3.3 | GPa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load | 1.80MPa | ISO 75-2 | 101 | °C |
Coefficient of Linear Thermal Expansion | | JIS K7197 | 6×10 | 1/℃ |
Vicat Softening Temperature | 50N | ISO 306 | 108 | °C |
Melt index | 230℃,37.3N | ISO 1133 | 5.5 | g/10min |
Specific Heat | | JIS K7123 | 1.5 | J/(g·℃) |
Spiral Flow | 厚薄2mm,250℃ | 三菱丽阳法 | 290 | mm |
Spiral Flow | 厚薄2mm,230℃ | 三菱丽阳法 | 180 | mm |
Thermal Conductivity | | JIS A1412 | 0.2 | W/(m·℃) |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Volume Resistivity | | JIS K6911 | >10 | Ωm |
Dissipation Factor | 60Hz | JIS K6911 | 0.05 | |
Insulation Resistance | 4kV/sec | JIS K6911 | 20 | MV/m |
Surface Resistivity | | JIS K6911 | >10 | Ω |
Dielectric Constant | 60Hz | JIS K6911 | 3.7 | |
Arc Resistance | | JIS K6911 | 没有痕迹 | |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | 24hr | ISO 62 | 0.3 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.