Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Refractive index of light | | ASTM D-542 | V|1.49 | |
Refractive index of light | | ASTM D-542 | MF|1.49 | |
Transmittance | 3.2mm | ASTM D-1003 | MF|93 | % |
Transmittance | 3.2mm | ASTM D-1003 | V|93 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Strength | 1/4″棒 | ASTM D-790 | MF|1100 | kg/cm2 |
Flexural Strength | 1/4″棒 | ASTM D-790 | V|1100 | kg/cm2 |
Notched Izod Impact Strength | 1/4″付 | ASTM D-255 | MF|1.7 | kg·cm/cm |
Notched Izod Impact Strength | 1/4″付 | ASTM D-255 | V|1.6 | kg·cm/cm |
tensile strength | | ASTM D-638 | MF|740 | kg/cm2 |
tensile strength | | ASTM D-638 | V|730 | kg/cm2 |
Tensile Strength | | ASTM D-695 | MF|1100 | kg/cm2 |
Tensile Strength | | ASTM D-695 | V|1100 | kg/cm2 |
Rockwell Hardness | | ASTM D-785 | MF|100 | M Scale |
Rockwell Hardness | | ASTM D-785 | V|95 | M Scale |
Tensile Elongation | | ASTM D-638 | MF|5 | % |
Tensile Elongation | | ASTM D-638 | V|5 | % |
Flexural Modulus | 1/4″棒 | ASTM D-790 | MF|3.2×104 | kg/cm2 |
Flexural Modulus | 1/4″棒 | ASTM D-790 | V|3.1×104 | kg/cm2 |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load | 18.56kg/cm2 | ASTM D-648 | MF|102 | °C |
Deflection Temperature Under Load | 18.56kg/cm2 | ASTM D-648 | V|92 | °C |
Coefficient of Linear Thermal Expansion | | ASTM D-696 | MF|6×10-5 | cm/cm/℃ |
Coefficient of Linear Thermal Expansion | | ASTM D-696 | V|6×10-5 | cm/cm/℃ |
Vicat Softening Temperature | 1kg | ASTM D-1525 | MF|116 | °C |
Vicat Softening Temperature | 1kg | ASTM D-1525 | V|107 | °C |
Specific Heat | | | MF|0.35 | cal/g/℃ |
Specific Heat | | | V|0.35 | cal/g/℃ |
Thermal Conductivity | | ASTM C-177 | MF|5×10-4 | Cal/s/cm/℃ |
Thermal Conductivity | | ASTM C-177 | V|5×10-4 | Cal/s/cm/℃ |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Volume Resistivity | | JIS K-6911 | MF|>1015 | |
Volume Resistivity | | JIS K-6911 | V|>1015 | |
Surface Resistivity | | JIS K-6911 | MF|>1016 | |
Surface Resistivity | | JIS K-6911 | V|>1016 | |
Dielectric Constant | 60Hz | | V|3.7 | |
Dielectric Constant | 60Hz | | MF|3.7 | |
Arc Resistance | | JIS K-6911 | MF|没有痕迹 | |
Arc Resistance | | JIS K-6911 | V|没有痕迹 | |
Dissipation Factor?(Tangent) | 60Hz | | MF|0.05 | |
Dissipation Factor?(Tangent) | 60Hz | | V|0.05 | |
Insulation Resistance | | | MF|20 | |
Insulation Resistance | | | V|20 | |
Processing | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | | ASTM D-955 | MF|0.2-0.6 | % |
Modeling Shrinkage | | ASTM D-955 | V|0.2-0.6 | % |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | 24hr | ASTM D-570 | MF|0.3 | % |
Moisture Absorption | 24hr | ASTM D-570 | V|0.3 | % |
Melt Mass-Flow Rate | 230℃,3.8kg | ASTM D-1238 | MF|2.0 | g/10min |
Melt Mass-Flow Rate | 230℃,3.8kg | ASTM D-1238 | V|2.5 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.