PA66 LUMID® GP2101BF KA02 LG CHEM KOREA

Unit Price:
$3006 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	24 hr, 23°C	ASTM D570	0.70	%
Modeling Shrinkage - Flow	23°C, 3.20 mm, Injection	ASTM D955	0.70 到 1.2	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Elongation	Break, 23°C, 3.20 mm, Injection	ASTM D638	3.0	%
Flexural Modulus	23°C, 3.20 mm, Injection	ASTM D790	4900	Mpa
Flexural Strength	23°C, 3.20 mm, Injection	ASTM D790	142	Mpa
Tensile Strength	Yield, 23°C, 3.20 mm, Injection	ASTM D638	98.1	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Coefficient of Linear Thermal Expansion (Flow)		ASTM D696	3.0E-5	cm/cm/°C
Peak Melting Temperature		ASTM D3418	260	°C
Deflection Temperature Under Load?	1.8 MPa, Unannealed, 6.40 mm, Injection	ASTM D648	230	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Comparative Tracking Index	Solution A	IEC 60112	250	V
Dielectric Strength	23°C, 1.00 mm	ASTM D149	22	KV/mm
Dielectric Constant	23°C, 1 MHz	ASTM D150	3.00
Volume Resistivity	23°C	ASTM D257	1.0E+14	ohms·cm

Injection	Test Result	Unit
Drying Temperature	80 到 100	°C
Suggested Max Moisture	0.10	%
Processing (Melt) Temp	270 到 290	°C
Mold Temperature	80 到 110	°C
Drying Time	4.0 到 5.0	hr
Rear Temperature	265 到 275	°C
Middle Temperature	270 到 280	°C
Front Temperature	270 到 285	°C
Nozzle Temperature	270 到 280	°C
Back Pressure	0.981 到 2.94	Mpa
Screw Speed	60 到 150	rpm

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R-Scale, 23°C, Injection	ASTM D785	120

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	0.8 mm	UL 94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.