Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | TD:3.00mm3 | 内部方法 | 0.60 | % |
| Modeling Shrinkage | MD:3.00mm4 | 内部方法 | 0.20 | % |
| Modeling Shrinkage | 吸水率(Equilibrium,23°C,50%RH) | 内部方法 | 1.8 | % |
| PVLimit-vs.S45C | | SuzukiMethod | 2.6 | MPa·m/s |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| AmountofWear-vs.S45C5 | | SuzukiMethod | 0.600 | mg/hr |
| Coefficient of Friction (vs.S45C) | | SuzukiMethod | 0.23 | |
| Tensile Stress | 23°C | ISO527-2 | 240 | Mpa |
| Tensile Strain | Break,23°C | ISO527-2 | 1.6 | % |
| Flexural Modulus | 23°C | ISO178 | 19000 | Mpa |
| Flexural Stress | 23°C | ISO178 | 335 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 250 | °C |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 2E-05 | cm/cm/°C |
| Melting temperature | | DSC | 265 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume Resistivity | | IEC60093 | 2.0 | ohms·cm |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.