PA66 LUMID® SG2460B KA30 LG CHEM KOREA

Unit Price:
$2514 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	24 hr, 23°C	ASTM D570	0.60	%
Modeling Shrinkage - Flow	23°C, 3.20 mm, Injection	ASTM D955	0.30 到 0.70	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Strength	Break, 23°C, 3.20 mm, Injection	ASTM D638	196	Mpa
Tensile Elongation	Break, 23°C, 3.20 mm, Injection	ASTM D638	3.0	%
Flexural Modulus	23°C, 3.20 mm, Injection	ASTM D790	11800	Mpa
Flexural Strength	23°C, 3.20 mm, Injection	ASTM D790	275	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Peak Melting Temperature		ASTM D3418	220	°C
Deflection Temperature Under Load?	1.8 MPa, Unannealed, 6.40 mm, Injection	ASTM D648	210	°C
Coefficient of Linear Thermal Expansion (Flow)		ASTM D696	3.0E-5	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength	23°C, 1.00 mm	ASTM D149	25	KV/mm
Dielectric Constant	23°C, 1 MHz	ASTM D150	4.00
Volume Resistivity	23°C	ASTM D257	1.0E+16	ohms·cm

Injection	Test Result	Unit
Drying Temperature	80 到 100	°C
Processing (Melt) Temp	270 到 295	°C
Mold Temperature	80 到 110	°C
Drying Time	4.0 到 5.0	hr
Rear Temperature	260 到 270	°C
Middle Temperature	270 到 285	°C
Front Temperature	270 到 290	°C
Nozzle Temperature	270 到 295	°C
Back Pressure	29.4 到 58.8	Mpa
Screw Speed	30 到 60	rpm

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R-Scale, 23°C, Injection	ASTM D785	120

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.