PA66 Ultramid® 8202HS BASF GERMANY
39
- Unit Price:
- $3311 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 45MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Modeling Shrinkage | MD:3.18mm | 1.2 | % | |
Moisture Absorption | 24hr | ASTMD570 | 1.6 | % |
23°C,24hr | ISO62 | 1.6 | % | |
Saturation | ASTMD570 | 9.5 | % | |
Saturation,23°C | ISO62 | 9.5 | % | |
Equilibrium,50%RH | ASTMD570 | 2.7 | % | |
Equilibrium,23°C,50%RH | ISO62 | 2.7 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Tensile Stress | Yield,-40°C | ISO527-2 | 126 | Mpa |
Yield,23°C | ISO527-2 | 78.0 | Mpa | |
Yield,80°C | ISO527-2 | 35.0 | Mpa | |
Yield,120°C | ISO527-2 | 25.0 | Mpa | |
Yield,150°C | ISO527-2 | 20.0 | Mpa | |
Tensile Strain | Yield,23°C | ISO527-2 | 4.0 | % |
Tensile Modulus | 23°C | ISO527-2 | 2700 | Mpa |
80°C | ISO527-2 | 485 | Mpa | |
120°C | ISO527-2 | 360 | Mpa | |
150°C | ISO527-2 | 290 | Mpa | |
Tensile Elongation | Yield,23°C | ASTMD638 | 4.0 | % |
Yield,80°C | ASTMD638 | 42 | % | |
Yield,121°C | ASTMD638 | 36 | % | |
Break,23°C | ASTMD638 | 55 | % | |
Flexural Modulus | -40°C | ASTMD790 | 3010 | Mpa |
23°C | ASTMD790 | 2830 | Mpa | |
65°C | ASTMD790 | 500 | Mpa | |
90°C | ASTMD790 | 350 | Mpa | |
121°C | ASTMD790 | 305 | Mpa | |
23°C | ISO178 | 2400 | Mpa | |
Flexural Strength | -40°C | ASTMD790 | 170 | Mpa |
23°C | ASTMD790 | 108 | Mpa | |
65°C | ASTMD790 | 30.0 | Mpa | |
90°C | ASTMD790 | 20.0 | Mpa | |
121°C | ASTMD790 | 17.0 | Mpa | |
Tensile Strength | Break,23°C | ASTMD638 | 75.0 | Mpa |
Yield,-40°C | ASTMD638 | 126 | Mpa | |
Yield,23°C | ASTMD638 | 79.0 | Mpa | |
Yield,80°C | ASTMD638 | 35.0 | Mpa | |
Yield,121°C | ASTMD638 | 25.0 | Mpa | |
Flexural Stress | 23°C | ISO178 | 85.0 | Mpa |
Nominal Tensile Strain at Break | 23°C | ISO527-2 | 25 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Peak Melting Temperature | ASTMD3418 | 220 | °C | |
RTIElec | 0.71mm | UL746 | 130 | °C |
1.5mm | UL746 | 130 | °C | |
3.0mm | UL746 | 130 | °C | |
6.0mm | UL746 | 130 | °C | |
Evolution Calendar intelligent importer | 0.71mm | UL746 | 95.0 | °C |
1.5mm | UL746 | 105 | °C | |
3.0mm | UL746 | 105 | °C | |
6.0mm | UL746 | 105 | °C | |
RTIStr | 0.71mm | UL746 | 95.0 | °C |
1.5mm | UL746 | 105 | °C | |
3.0mm | UL746 | 105 | °C | |
6.0mm | UL746 | 105 | °C | |
Linear thermal expansion coefficient | MD | ASTME831 | 8.3E-05 | cm/cm/°C |
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ASTMD648 | 178 | °C |
0.45MPa,Unannealed | ISO75-2/B | 150 | °C | |
1.8MPa,Unannealed | ASTMD648 | 65.0 | °C | |
1.8MPa,Unannealed | ISO75-2/A | 60.0 | °C | |
Melting temperature (DSC) | ISO3146 | 220 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Volume Resistivity | IEC60093 | >1.0E+13 | ohms·cm | |
Comparative Tracking Index | IEC60112 | 600 | V | |
Dielectric Strength | IEC60243-1 | 37 | KV/mm | |
Volume Resistivity | 1.50mm | ASTMD257 | >1.0E+13 | ohms·cm |
Dielectric Strength | 1.50mm | ASTMD149 | 22 | KV/mm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Drop Impact Resistance | 23°C | 内部方法 | 142 | J |
Charpy Unnotched Impact Strength | -30°C | ISO179 | 51 | kJ/m² |
23°C | ISO179 | NoBreak |
hardness | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Rockwell Hardness | R-Scale | ASTMD785 | 119 |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
UL flame retardant rating | 0.71mm | UL94 | V-2 | |
1.5mm | UL94 | V-2 | ||
3.0mm | UL94 | V-2 | ||
6.0mm | UL94 | V-2 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.