Technical Data Sheet
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Yield | ISO 527-2/50 | 70.0 | Mpa |
Tensile Strain | Break | ISO 527-2/50 | 45 | % |
Tensile Modulus | | ISO 527-2/1 | 2900 | Mpa |
Flexural Modulus | | ISO 178 | 2400 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Vicat Softening Temperature | | ISO 306/B50 | 235 | °C |
Deflection Temperature Under Load? | 0.45 MPa, Unannealed | ISO 75-2/B | 195 | °C |
Deflection Temperature Under Load? | 1.8 MPa, Unannealed | ISO 75-2/A | 80.0 | °C |
Melting temperature | | ISO 11357-3 | 262 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC 60093 | 1.0E+13 | ohms |
Volume Resistivity | | IEC 60093 | 1.0E+15 | ohms·cm |
Injection | Test Condition | Test Method | Test Result | Unit |
---|
Drying Temperature | | | 75 到 85 | °C |
Processing (Melt) Temp | | | 265 到 285 | °C |
Mold Temperature | | | 70 到 120 | °C |
Drying Time | | | 2.0 到 4.0 | hr |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R -Sale | ISO 2039-2 | 118 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Burning Rate | | FMVSS 302 | < 100 | mm/min |
Flame Rating | 0.8 mm | UL 94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.