Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD:24hr | ASTMD955 | 0.15 | % |
Modeling Shrinkage | TD:24hr | ASTMD955 | 0.17 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
fracture | | ISO527-2/5 | 75.0 | Mpa |
fracture | | ISO527-2/5 | 0.90 | % |
Break | | ASTMD638 | 1.0 | % |
50.0mm Span | | ASTMD790 | 12400 | Mpa |
--5 | | ISO178 | 14000 | Mpa |
--6 | | ISO178 | 90.0 | Mpa |
--1 | | ASTMD638 | 10800 | Mpa |
Break | | ASTMD638 | 54.0 | Mpa |
Break,50.0mm Span | | ASTMD790 | 78.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flow:-40 to 40°C | | ASTME831 | 1.6E-05 | cm/cm/°C |
Flow:23 to 80°C | | ISO11359-2 | 1.6E-05 | cm/cm/°C |
Flow:-40 to 40°C | | ASTME831 | 3.6E-05 | cm/cm/°C |
Flow:23 to 80°C | | ISO11359-2 | 4.8E-05 | cm/cm/°C |
Flow:-30 to 80°C | | ISO11359-2 | 1.4E-05 | cm/cm/°C |
Flow:-30 to 80°C | | ISO11359-2 | 4E-05 | cm/cm/°C |
--11 | | ASTM D790/ISO 178 | 3.5 | W/m/K |
--12 | | ASTM D790/ISO 178 | 15 | W/m/K |
--13 | | ISO22007-2 | 1.5 | W/m/K |
--14 | | ISO22007-2 | 18 | W/m/K |
1.8MPa, Unannealed,3.20mm | | ASTMD648 | 186 | °C |
1.8MPa, Unannealed,64.0mm Span | | ISO75-2/Af | 200 | °C |
Ball PressureTest | 165°C | IEC60695-10-2 | Pass | |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | ASTMD257 | 3E+05 | ohms |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
23°C8 | | ISO180/1A | 3.0 | kJ/m² |
23°C9 | | ISO180/1U | 8.0 | kJ/m² |
23°C | | ASTMD4812 | 150 | J/m |
23°C | | ASTMD256 | 26 | J/m |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 1.00mm | UL94 | HB | |
Glow Wire Flammability Index | 1.00mm | IEC60695-2-12 | 850650 | °C |
Glow Wire Flammability Index | 1.60mm | IEC60695-2-12 | 960 | °C |
Glow Wire Ignition Temperature | 1.00mm | IEC60695-2-13 | 825 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.